고크롬 롤의 수명과 마멸특성에 관한 연구

A Study on the Wear Characteristics and Lifetime Of High Chromium Roll

Work rolls used in cold rolling mills must have outstanding wear resistance and very little plastic defor- mation. Thus, these rolls require a higher surface hardness and harding to a greater depth. To meet these requirements, the rolls, in general, have basic chemical composition of 0.7 to 1.0% carbon and 1.0 to 5.0% Cr(chromium), plus a small amounts of special elements, and are subjected to intensive water quenching and tempering at low temperature to provide a surface hardness of over 90 shore. This test results are as follows. Deflection and fracture load of 5% Cr material are than those of 3% Cr material and show flat curve from surface to subsurface. It will be clear that 5% Cr work roll has a superior resisti- bility against wear and abrasion comparing with 3% Cr work roll. The improvement of wear and abrasion in 5% Cr work roll will be achieved by the large amount of wpheroidal carbide. In grindability and polish, 5% Cr work roll will be a little inferior comparing with 3% Cr work roll.