Abstract
Variations of core loss and coercivity with heat treatment condition have been studied in amorphous ribbon core specimens. All measurements were performed at 10 kHz with a maximum induction of 0.1 T. With increasing annealing time, both core loss and coercivity of core specimens decreased first, reaching minimum values, and increased thereafter. Specimen heat treated in an air showed better soft magnetic properties than those treated in Ar atmosphere. The specimens annealed under magnetic field higher than 6 Oe in radial direction showed reduced core loss and coercivity. The field annealing effects were increased with increasing cooling rate near Curie temperature of the material. The specimen annealed under an applied field in perpendicular direction of the core showed increased coercivity and decreased permeability.
비정질 리본으로 제조된 링 코아 시편의 자장중 열처리 조건에 따른 철손 및 보자력 등의 연자기 특성 변화를 BH loop tracer를 이용하여 최대인가자기유도 0.1 T를 유지하면서 10 kHz에서 측정하였다. 열처리 시간이 증가함에 따라 코아의 철손 및 보자력은 감소하여 최소값에 도달한 다음 다시 증가한다. 공기 중에서 열처리한 경우의 시료가 Ar 분위기에서 열처리한 시료 보다 우수한 연자기 특성을 나타낸다. 코아의 원주방향으로 자장을 인가한 경우에는 인가자장의 세기가 6 Oe 이상이어야 자장중 열처리 효과가 나타나 철손 및 보자력이 감소하였으며, 냉각시 Curie 온도근처에서의 냉각속도가 빠를 수록 철손과 보자력은 감소한다. 코아의 폭 방향으로 자장을 인가한 경우에는 보자력의 증가와 투자율의 감소 및 약간의 철손 증가가 나타났다.