Abstract
$Cu_{0.9}Ni_{0.1}Fe_2O_4$ has been studied with Mossbauer spectroscopy and X-ray diffraction. The crystal structure is found to be a cubic spinel with the lattice constant $a_0=8.386{\AA}$. The Curie temperature is determined to be $T_c=755K$ for a heating rate of 5 K/ min. The Mossbauer spectra consist of two six-line patterns corresponding to $Fe^{3+}$ at the tetrahedral(A) and octahedral(B) sites. Debye temperatures for A and B sites are found to be 568 k and 194 K, respectively. Atomic migration of $Cu_{0.9}Ni_{0.1}Fe_2O_4$ begins near 350 K and increases rapidly with increasing temperature such a degree that 71% of the ferric ions as A sites have moved over to the B sites at 550 K.
$Cu_{0.9}Ni_{0.1}Fe_{2}O_{4}$의 결정학적 및 자기적 성질을 Mossbauer 분광법과 X-선 회절법으로 연구하였다. 결정구조는 입방 spinel구조 갖으며, 격자상수 $a_{0}$ = 0.386 .angs. 임을 알았다. 또한 thermal scan 방법에 의해 Curie 온도 $T<_{c}$ = 755 K로 결정하였다. 이성질체 이동결과 사면체(A) 자리와, 팔면체 (B) 자리 모두 철이온의 전하상태가 +3가 임을 알았다. A, B 자리의 Debye 온도는 각각 568 K 와 194 K 임을 알았다. 또한 $Fe^{+3}$ 이온이 A 자리에서 B 자리로의 원자이동은 350 K 근처에서 시작되었으며, 온도 증가에 따라 급격히 증가하여 550 K 에서 Fe 이온의 이동률은 71 % 이었다.