Abstract
An experimental research was carried out to investigate the effect of thc compressive strength of concrete on the stirrup effectiveness in shear behavior of concrete beams. For this purpose. total 24 beams of section dimension of $300{\times}600mm$ were tested: 4 specimens without web reinforcement and 20 specimens with web reinforcement in the form of vertical stirrups. Main variables were two levels(norma1 and high strength) of the compressive strength of concrete and six types of t h e shear rcinfor.cement ratios. Prior to experiment, for given sections and assumed material constants, the reference shear reinforcement ratio(${\rho}_vACI$) which leads to the flexure failure using the provisions of the ACI Building Code(AC1 318-95) was calculated. and the shear reinforcement ratios were relatively selected from the value of ${\rho}_vACI$. From test results, it was shown that thc safety factor of ACI eyuation for p1,ediction of shear strength was decreased with increasing the compressive strength of concrete in beams without stirrups. However. it was observed that as the amount of' stirrup is increased, the safety factor for high strength conci,ete beams with high stirrup ratio is ensured more than that for normal strength concrete beams. Therefore i t appears that the stirrup effectiveness of high strength concrete beams is greater than that of normal strength concrete beams.
이 연구에서는 콘크리트 보의 전단거동에서 콘크리트 압축강도가 스터럽 유효성에 미치는 영향을 실험적으로 연구하였다. 이를 위하여 단며이 $300{\times}600mm$ 인 수직 스터럽이 배근되지 않은 콘크리트 보 4개와 수직 스터럽이 배근된 콘크리트 보 20개에 대하여 실험을 수행하였다. 주요 실험변수는 2종류(보통강도, 고강도)의 콘크리트 압축강도 수준과 6종류의 전단철근비이다. 실험에 앞서 주어진 단면과 가정된 재료 상수에 대하여 ACI Building Code를 사용하여 휨파괴가 유발되는 전단철근비( ${\rho}_vACI$)를 산정하였으며, 이 값을 기준으로 6종류의 전단철근비를 선택하였다. 실험결과, 스터럽이 배근되지 않은 콘크리트 보에 있어서 ACI 전단강도식의 안전율은 콘크리트의 압축강도가 증가함에 따라 감소하는 것으로 나타났다. 그러나 스터럽이 많이 배근된 고강도 콘크리트 보에서는 보통강도 콘크리트 보 이상의 안전율이 확보되는 것으로 나타나 스터럽 유효성은 고강도 콘크리트 보에서 더 큰 것으로 나타났다.