A Study on the Fundamental Properties of Cement Mortar Using Polymer Coated Crumb Rubber

폴리머 코팅 폐타이어 분말을 혼입한 시멘트 모르터의 기초적 성질

Recently, the disposal of used vehicle tires is a big social problem because the amount of used vehicle tires has been increased with development of' automobile industry. Many researches have been made on the recycling of used vehicle tires in the various fields of industry as well as construction industry. When the crumb rubber made of vehicle tires is mixed in cement concrete and mortar, it is indicated that the adhesive strength of interface between the crumb rubber and cement hydrates is very low. The purpose of this study is to improve the fundamental properties by increasing of the adhesion strength of styrene-butadiene rubber(SF3R) latex coated crumb rubber in ; cement mortar. SBR-modified mortar using crumb rubber is also tested as the same method. From the test results, the cement mortar using SBR latex coated crumb rubber have a good fundamental properties compared with that using uncoated crumb rubber. The mechanical properties of SBR-modified mortar using crumb rubber with polymer-cement ratios of 10% are also improved.

최근 많은 양의 폐타이어가 발생됨에 따라 사회적 문제로 대두되고 있는 실정이며, 이에 대한 재활용은 각 분야에서 활발하게 연구되고 있다. 건설 분야에서는 폐타이어를 냉각 분쇄하여 만든 분말을 시멘트 콘크리트에 혼입하여 사용하는 연구가 많이 수행되고 있다. 시멘트 콘크리트에 폐타이어 분말을 혼입하여 사용할 때는 폐타이어 분말과 시멘트경화체 사이에서 접착성의 문제로 기초적 성질이 저감된다. 본 연구에서는 시멘트 모르터 내부에서 폐타이어 분말의 접착력을 증진시키기 위하여 시멘트 혼화용 폴리머 중의 하나인 스티렌 부타디엔 고무(SBR)라텍스를 사용하여 기초적 성질을 개선하고자 하였다. 실험결과 SBR 코팅 폐타이어 분말을 혼입한 시멘트 모르터는 코팅하지 않은 폐타이어 분말을 사용한 경우보다 기초적 성질이 개선되는 것으로 나타났으며, 또한 폴리머 시멘트비 10%를 사용한 SBR 라텍스 혼입 폴리머 시멘트 모르터의 경우에도 기초적 성질이 개선되었다.