Abstract
Sol-Gel derived ferroelectric Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ thin films have been fabricated on Pt/Ti/ $SiO_{2}$/Si substrate. Two kinds of fast annealing methods, F-I (six times of intermediate and final annealing) and F-II(one final annealing after six times of intermediate annealing) were used for preparation of multi-coated PZT thin films. As the annealing temperature was increased, high capacitance could be obtained, for instance, 2700.angs.-thick PZT thin film annealed at 680.deg. C had a capacitance value of approximately 20nF at 1kHz. In addition, it is found that the dielectric constant is a function of the perovskite phase fraction. In case of F-I method, PZT thin film had a remanent polarization(Pr) of 8-15.mu.C/c $m^{2}$ and a coercive field( $E_{c}$) of 35-44kV/cm according to annealing temperature, whereas PZT film fabricated by F-II method had as high as 24-25.mu.C/c $m^{2}$ and 48-59kV/cm, respectively. As a result of measuring Curie temperature, PZT thin film had a range of 460-480.deg. C by F-I method and more or less higher range of 525-530.deg. C by F-II method, which implied that different microstructures could cause the different Curie temperature. Through I-V measurement, leakage current of PZT thin film fabricated by F-I and F-II methods was 64nA/c $m^{2}$ and 2.2.mu.A/c $m^{2}$ in the electric field of 100kV/cm, respectively.y.y.y.