Study on the whitening phenomenon on inside of glass bottle by surface analysis methods

표면분석에 의한 유리 용기내의 백색현상 연구

It has been found that an white precipitates at the inside surface is a common characteristics of soda-lime-silica glasses which have not undergone special surface treatments during hot weather season. In this study, the white deposits were examed using by solution method, surface analysis etc., and the dependence of weathering on the atmospheric condition was also investigated. As a results, the white precipitates on the glass surface was discorved as carbonates like $Na_2CO_3{\cdot}H_2O,CaCO_3$. Coming to atmosphere-dependence, it was shown that the glass made and stored at sea shore province had 3 times much severe weathering than that at land province.

하절기에 장시간 창고에 보관된 일반 소다-라임-실리케이트 유리는 특별한 표면처리를 하지 않는 한 백색물질이 표면에 석출되는 weathering 현상이 나타날 수 있다. 본 연구는 유리병 내벽 표면에 생성된 백색물질을 습식법 및 표면분석법 등을 이용하여 분석하고 대기의 변화에 따른 weathering 정도를 연구하였다. 표면에 석출된 백색의 물질은 육각관상의 Na$_2$CO$_3$${\cdot}$H$_2$O와 CaCO$_3$로 규명되었다. 해안지방에서 제조-보관되었던 유리병 표면은 내륙지방의 유리병에 비해 weathering된 깊이가 3배 정도로 그 정도가 심하여 weathering이 대기중의 수분량에 크게 의존함을 알 수 있었다.