유구치 아말감 수복물에서 레진 접착성 이장재의 미세 변연 누출에 관한 비교 연구

AN EXPERIMENTAL STUDY FOR MICROLEAKAGE OF AMALGAM USING RESIN ADHESIVE LINERS IN PRIMARY MOLAR TOOTH

The purpose of this study was to compare the marginal leakage of resin liner which was used as a liner to amalgam restoration. Control group composed of no liner group, copalite group and experimental group composed of All-bond 2, Vitrebond, Superbond D-liner applied groups were evaluated. Cl.V preparation with a size of $3{\times}2{\times}1.5mm$ on 70 extracted primary molars were made and applied appropriate liners for each groups. After amalgam filling and polishing, polished specimens underwent temperature changed from $5^{\circ}C\;to\;55^{\circ}C$ a thousand times. After thermocycling, specimens were placed in 2% methylene blue dye solution for 72 hours in an incubator set at $37^{\circ}C$. The teeth were sectioned buccolingually and the degree of dye penetration was observed with a spectroscopy. (${\times}30$) The following results were obtained. 1. Vitrebond, All-bond 2, Superbond D-liner group exhibited a statistically significant lower degree of dye penetration than no liner and copalite group. (Kruskal-Wallis analysis, P<0.05) 2. No liner group and copalite group exhibited a similar degree of dye penetration. (Mann-Whitney analysis, P>0.05) 3. All-bond 2 group exhibited a statistically significant lower degree of dye penetration than Vitrebond group, (Mann-Whitney analysis, P<0.05) Superbond D-liner group also exhibited a lower degree of dye penetration than Vitrebond group but was statistically insignificant. (Mann-Whitney analysis, P>0.05)