Abstract
To improve photosensisitizing efficiency of ZnO/$H_2Pc(I)_x$ system, ZnO/$H_2Pc(I)_x$ system was dispersed in a typical photoconductive polymer of poly(9-vinylcarbazole)(PVCZ). The iodine dopant level(x) of ZnO/${\chi}-H_2Pc(I)_x$ is proportional to concentration of iodine, whereas x of ZnO/${\beta}-H_2Pc(I)_x$ decreased from the highest x=0.97 at more than $6.3{\times}10^{-3}$ M iodine solution. The Raman spectra of ZnO/${\chi}-H_2Pc(I)_x$ at 514 nm exhibited characteristic $I_3^-$ patterns in the range of 50∼550 $cm^{-1}$ at $x{\geq}0.57.$ The surface photovoltage of ZnO/${\chi}-H_2Pc(I)_{0.48}$/PVCZ was approximately 1.6 times greater than ZnO/${\chi}-H_2 Pc(I)_{0.48}$ and was 1.8 times of ZnO/${\chi}-H_2Pc(I)_{0.57}$/PVCZ at 670 nm. With ZnO/$H_2Pc(I)_x$/PVCZ, the highest iodine dopant levels showed a higher photovoltage. Therefore the injection of holes from H2Pc into PVCZ resulted in that photosensisitizing effect of ZnO/$H_2Pc(I)_x$/PVCZ system was improved compared to ZnO/$H_2Pc(I)_x$ case.
ZnO/$H_2Pc(I)_x$계의 광증감성 효율을 높이기 위하여 ZnO/$H_2Pc(I)_$x를 광전도성 고분자인 poly(9-vinylcarbazole)(PVCZ)에 분산시켰다. $H_2Pc$ 결정형에 따른 ZnO/$H_2Pc(I)_x$계의 요오드 도핑 함량(x)은 ZnO/${\chi}-H_2 Pc(I)_x$ 경우는 요오드의 농도가 증가할수록 x값이 증가하였고, ZnO/${\beta}-H_2Pc(I)_x$ 경우는 약 x=0.95인 요오드 농도가 $6.3{\times}10^{-3}\;M$ 이후에서는 오히려 x값이 감소되었다. 514.5 nm로 여기시킨 ZnO/${\beta}-H_2Pc(I)_x$계의 라만 스펙트럼에서 x값이 약 0.57에서부터 $I_3^-$ chain에 대한 특성 피크가 50~550 $cm^{-1}$에서 나타나기 시작하였다. ZnO/{\chi}-H_2Pc(I)_{0.48}$/PVCZ의 광증감 효과는 ZnO/${\chi}-H_2Pc(I)_{0.48}보다 1.6배, ZnO/${\beta}-H_2Pc(I)_{0.57}$/PVCZ보다 1.8배 크게 나타났다. 그리고 ZnO/$H_2Pc(I)_x$/PVCZ계에서 x값이 증가될수록 광중감 효과도 크게 증가되었다. 그러므로 $H_2Pc$의 광여기로 생성된 정공이 PVCZ으로 주입되어 ZnO/$H_2Pc(I)_x$/PVCZ계의 광증감 효과가 ZnO/$H_2Pc(I)_x$계의 광중감 효과보다 향상되는 것으로 판단된다.