Abstract
The magnetic properties of Nd-Fe-B alloys of containing 4 at.% Nd have been studied for the development of new type rare-earth magnets. The amorphous phase of a melt-spun $Nd_{4}Fe_{85.5}B_{10.5}$ alloy is transformed into the phases which have a small amount of $Nd_{2}Fe_{14}B_{1}$ in ${\alpha}-Fe$ matrix by annealing above their crystallization temperature. The addition of Mo, Nb, V or Cu to $Nd_{4}Fe_{85.5}B_{10.5}$ alloy results in the reduction of grain size and the sub¬sequent improvement of the coercivity. The coercivity of $Nd_{4}Fe_{82}B_{10}M_{3}Cu_{1}$(M = Mo, Nb, V) alloys increases in the order of M = V < Nb < Mo and shows the highest value of 2.7 kOe when M = Mo. On the other hand, the rem¬anence of these alloys shows the opposite trend and the rn>st improved value of 1.35 T is observed when M = V.
Nd 함유량을 4 at.%로 고정시킨 Nd-Fe-B 합금의 자기특성이 조사되었다. 급속응고된 $Nd_{4}Fe_{85.5}B_{10.5}$ 합금은 열처리에 의하여 ${\alpha}-Fe$ 연자성기지에 석출되며, $Nd_{4}Fe_{85.5}B_{10.5}$ 합금에 Mo, Nb, V 및 Cu의 첨가는 결정립을 미세화시켜 보자력을 향상시킨다. 그러나 ${\alpha}-Fe$ 결정립에 의한 각형성 열화는 잔류자화를 감소시킨다. $Nd_{4}Fe_{82}B_{10}M_{3}Cu_{1}$(M = Mo, Nb, V) 합금에서 보자력은 M = V < Nb < Mo로 증가하며, M = Mo에서 2.7 kOe이고, 잔류자화는 M = Mo < Nb < V순으로 증가하며 M = V에서 1.35 T이다.