EFFECT OF VARIOUS MECHANICAL TREATMENTS ON TITANIUM PLASMA SPRAYED IMPLANT SURFACES

Titanium plasma sprayed implant에 관한 여러가지 기계적 표면처리방법이 implant표면조도에 미치는 영향

For maintenance of an ailing or failed implant it is essential to treat the implant fixture surface so as to remove bacterial endotoxin and make a surface tolerated by surrounding soft and hard tissue. Thus in this study the method that makes the smoothest surface treated with a high speed diamond bur, a low speed diamond bur, a stone, a rubber point or Jetpolisher was studied. With the profilomenter a mean value of $R_{max}$ was measured. The hight speed diamond, the rubber point and the Jetpolisher showed a mean $R_{max}\;7.77{\mu}m$. The low speed diamond bur, the rubber, point and the Jetolisher made a mean value of $R_{max}\;8.44{\mu}m$. The stone, the rubber point and the Jetolisher showed the smoothest surfaces with a mean value of $R_{max}\;6.24{\mu}m$. TPS (titanium plasma sprayed) areas showed a mean vlaue of $R_{max}\;24.42{\mu}m$, and the smooth surfaced titanium disc manufactured by the company (IMZ, Germany) shows a mean value of $R_{max}\;3.00{\mu}m$. Under the SEM examination the disc treated with a high speed diamond bur, a rubber point and a Jetpolisher showed partially remaining TPS particles, but the height of these particles were reduced remarkably compared with those of the original TPS. The disc treated with a low speed diamond bur, a rubber point and a Jetpolisher showed a rough topography with remaining TPS on the entire surface. A stone, a rubber point and a Jetpolisher removed almost TPS and the bulk titanium metal was exposed and some scratches were made by the stone. All treated discs were revealed as rougher than the smooth surface disc manufactured by the company. An untreated TPS disc shows a very irregular surface and a $40{\mu}m$ height of the plasma sprayed areas.

실패한 임프란트를 구강내에 유지하기 위하여는 임프란트 매식체의 표면을 처치하여 세균독소를 제거하구 주위의 연, 경조직에 적합한 표면 구조를 만들어 주어야 한다. 이에 본 연구에서는 임프란트 매식체 표면을 high speed diamond bur, low speed diamond bur, stone, rubber point, Jetpolisher로 처치하여 가장 평활한 표면을 만들 수 있는 방법을 알아 보았다. 조도측정기를 이용하여 표면의 최대높이값을 측정한 결과 high speed diamond bur, rubber point, Jetpolisher를 사용한 시편의 최대높이값의 평균은 $7.77{\mu}m$였고, low speed diamond bur, rubber point, Jetpolisher를 사용한 경우에는 $8.44{\mu}m$를 보였다. Stone, rubber point, Jetpolisher를 사용한 경우 $6.24{\mu}m$로 가장 평활한 표면을 보였다. 이러한 수치들은 제거하지 않은 TPS(titanium plasma sprayed)면의 $24.43{\mu}m$에 비하여는 낮은 수치를 보였다. 주사전자현미경으로 관찰 하였을 때 high speed diamond bur, rubber point, Jetpolisher를 사용한 군에서는 TPS 입자들이 부분적으로 남아있었으나 이 입자들은 그 높이가 원래의 TPS에 비하여는 상당히 감소되어 있었다. Low speed diamond bur, rubber point, Jetpolisher를 사용한 시편에서는 전 표면에 걸쳐 TPS가 남아있는 거친 표면 구조를 보였다. Stone, rubber point, Jetpolisher를 사용한 시편은 대부분의 TPS가 제거되어 titanium이 노출되어 있었고, titanium 금속에 stone에 의한 흠들이 보였으나 일부분에서는 TPS가 남아있어 제조회사에서 만들어진 평활한 표면에 비해서는 거친 양상을 보였다.