Abstract
Hydrogenation on the top gate and bottom gate Poly-Si TET's was performed by using Nh$_{3}$ plasma and annealing SiN film deposited by PECVD and then the electric characteristics on Poly-Si TET were investigated. As the time of NA$_{3}$ plasma treatment increaes, on/off current ratio gradually increases and the swing value decreases. The trap densities of graim boundaries in Poly-Si decrease very much during the inital 20min of hydrogenation time, and the decreasing scale becomes smaller after 20 min. The electric characteristics of the top gate TFT are better than those of the bottom gate TFT, it is considered due to the defects at the interface between the Poly-Si and the underlayer, SiO$_{2}$. After NH$_{3}$ plasma was treated for 2 hours for the top gate TFT, as the aging time atroon temperature increases on current was not scacely changed and off current decreases more than 1 order. Gate current density recovers to original value after the aging treatment for 8 days and then the electric characteristics are finally improved. It is suggested that the degraded characteristics of gate oxide are improved, from the variations of C-V characteristics with aging time. For the hydrogenation of isothermal and isochronal annealing SiN film deposited by PECVD, the characteristics of Poly-Si TFT are improved with increasing annealing temperature and are not largely changed with increasing annealing time. This results is good in agreement with the hydrogen reduction in Sin film as variations of annealing temperature and time.