T.M.C.P. 강의 부식피로거동에 미치는 염분의 영향에 관한 연구

The Study on the Influence of the Concentration NaCl Solution on Corrosion Fatigue Behavior of T.M.C.P. Steel

  • 이상호 (동아대학교, 해양공학과) ;
  • 한정섭 (동아대학교, 해양공학과)
  • 발행 : 1993.12.01

초록

To study the corrosion fatigue begavior of T.M.C.P. steel, the rotary bending fatigue test with the change of concentration of NaCl solution was carried out. Fatigue life in the corrosion environment is decreased markedly in comparision with that in the air. Fatigue limit in the air was about 225 MPa. In case of 3.5% NaCl solution fatigue life could be expressed as .sigma./sub f/=10,392 * (N/sub f/)/sup -o.2923 . According to the paris's rule, crack growth rates could be expressed as da/dN=2.62.*10/sup -7/ .DELTA. K/sup 1.09/(3.5% NaCl solution), da/dN=1.95 *10/sup -7 .DELTA. K/sup 1.05/(1% NaCl solution), da/dN=2.62 * 10/sup -7/.DELTA./sup 0.72/(0.01% NaCl solution) with da/dN expressed in mm/cycle and .DELTA.K in MPa.GAMMA.m. The crack growth rate in the corrosion environment was highest under 3.5% NaCl solution.

키워드

참고문헌

  1. 대한용접학회지 v.8 no.2 TMCP 고장력강 용접부의 피로 특성에 관한 연구 임채범 외 3명
  2. 대한용접학회지 v.8 no.4 TMCP 고장력강과 그 용접부의 저사이클피로특성에 관한 연구 김영식 외 1명
  3. 日本機械學會論文集(A 編) v.55 no.510 Fatigue Crack Characteristics of Four 50kg/mm² TMCP Steels and Their Weld-Heat-Affected-Zone in Synthetic Sea Water at a Frequecny of 0.1 Hz M.Kaname;O.Akio
  4. Kwasaki Steel Technical Report v.13 Fatigue Properties of 50 kg/mm² High-Strength Hull Structural Manufactured by Thermomechanical Control Process M.Shigeto;N.Asao
  5. Iro steel Inst. Jpn. Corrosion Fatigue Crack Growth Characteristics of a 50kg/mm² TMCP Steel in Synthetic Sea Water K.Kenjiro;M.Kohji
  6. 대한금속학회지 v.30 no.4 TMCP형 600MPa 급 건축용강에서 미세조직조절에 의한 항복비 개선 이상우;주웅용
  7. Corrosion and Corrosion Control Uhlig,H.H.
  8. JSME Bulletin v.20 no.143 Environment Effects in Initiation and Propagation of Fatigue Crack K.Endo;K.Komai
  9. Corroision Fatigue Barson,J.M.
  10. 변형 및 파괴역학 이동녕;김정수;이성근
  11. 대한기계학회지 v.29 no.2 부식피로 권영각
  12. Metal v.34 no.385 Limitation of Linear Elastic Fracture Mechanics for Growing Small Fatigue Cracks and Its Depenedence in Microstructure K.ToKaji;T.Ogawa;Y.Harada;Z.Ando
  13. Metal v.35 no.391 Evaluation of Limits of Linear Elastic Fracture Mechanics for Small Fatigue Cracks under Rotating Bending K.Tokaji;T.Ogawa;Y.Marada