Experiments for the Fatigue Behavior of High Strength Concrete

고강도 콘크리트의 피로거동에 관한 실험적 연구

In thls study, cylindrical concrete specimens wth varlous strength levels were tested to lnves tlgate the fatigue behavlor of high strength concrete. Selected test variables welp cornpresslve strength with 4 levels(26 MIPa, 54 MPa, 82 MPa. 103 MPa) and maximum \tress wlth 4 levels (75% 80%, 85%, 95%). A total of 160 specimens(${\phi}100{\times}200mm$) were cdsted fol the test. l'he fatigue llfe was decreased for the hlgher strength concreate. R model fol S N, relationship con sidering the effect of compressive strength, was proposed. In addition, this model included the stram rate effect whlch was modified for the strength level. It was found that the ~rrecoverable stram of normal strength concretc3 was greater than that of high strength concrete However the strain ~ncrease per cycle of load was great for the highcr strength concrete.

본 연구에서는 콘크리트의 강도수준에 따른 피로실험을 수행하여 고강도 콘크리트의 피로거동 특성을 분석하였다. 실험변수는 4종류의 강도수준(26 MPa, 54 MPa, 82 MPa, 103 MPa)과 4종류의 최고 응력수준(75%, 80%, 85%, 95%)이며 실험에 사용된 공시체는 ${\phi}100{\times}200mm$의 원통형 공시체로서 총 160개가 제작되었다. 실험결과, 강도수준이 증가함에 따라 피로강도가 감소하였고 강도수준의 영향을 고려한 S-N-f'c 관계식을 제안하였다. 또한 강도수준의 영향 이외에도 변형도율 효과를 도입하여 피로실험과 압축실험에서 발생하는 하중재하율의 차이를 보정하였다. 한편, 피로 비탄성변형도는 강도수준이 증가함에 따라 감소하였으나 반복횟수에 따른 변형도 증가율은 강도수준이 높을수록 큰 것으로 나타났다.