Phases and phase Equilibria of the Pt-Sb System

백금-안티모니 계의 식평구 및 화합흉에 대한 연구

The phase diagram of the Pt-Sb system was reinvestigated, using the conventional sealedcapsule technique. The identification of phases present in the reaction products was made by reflected light microscopy, X-ray diffraction and electron microprobe analysis. The existence of compounds, Pt5Sb, Pt3Sb, Pt3Sb2, PtSb and PtSb5 was confirmed. A new phase, Pt5Sb with a composition of 83at% Pt and tetragonal structure of the lattice parameters a=3.948(3), c=16.85(1)A, was found. The X-ray powder data of Ptsb may be indexable on a tetragonal cell with a=3.9455(7), c=16.959(5)A. PtSb is stoichiometric up to 800t and becomes Pt-deficient as much as lat% at 1000t. Solid solubility limits of Sb in Pt were determined to be 7.5,10.0 and 6.1at% at 1000˚,800˚ and 600˚ , respectively. The earlier reported Pts Sbf was not found in this study. The liquidus curve between the Ptsb2 and Sb phases was revised.

백금-안티모니갔의 상평형 및 안정 화합물에 대한 연구를 위해 합성실험을 실시하였다. 반응생성물은 반 사현미경, X-선 회절분석, 전자현미분석 등으로 규명하 였다. 백금-안티모니계에는 Pt5Sb, Pt3Sb, Pt3Sb2, PtSb, PtSb5등 5종류의 화합물이 존재하며 Pt5Sb2는 존재하지 않는 것으로 밝혀졌다. Pt5Sb는 처음 발견된 화합물로서 83at.%Pt의 화학성분을 가지며, 정방정계와 격자상수 a=3.948(3), c=16.85(1)차를 가진다. Ptssb 의 X-선회절 분말자료는 a=3.9455(7), c=16.959(5) A 인 정방정계의 구조로 격자지수화가 가능하다. PtSb의 화학성분은 800연까지 50at.% Pt이나 10반종에서는 49at.%정 회이다. 백금속의 안티모니 고용한계는 1000°, 800°, 600°에서 각각 7.5, 10.0, 6.1at.%이다. Ptsb2와 Sb를 잇는 액상곡선의 형태도 수정되었다.