구상흑연주철의 Mn성분과 펄라이트-베이나이트변태 처리의 변화가 미세조직에 미치는 영향

Changes of Microstructure due to Mn Element and Pearlite-Bainite Transformation Treatment in Ductile Cast Iron

The purpose of present investigation is to obtain ductile cast iron with ferrite-bainite matrix by pearlite-bainite transformation treatment. Ductile cast irons having three kinds of Mn ampunt had been manufactured. Mn increased pearlite volume fraction iin as-cast ductile cast iron. Ductile cast irons of different pearlite fraction were austenitized at $875\;^{\circ}C$ for 230-350 sec or $925\;^{\circ}C$ for 130-170 sec followed by austempering at $300\;^{\circ}C$ or $400\;^{\circ}C$ for the various periods of time from 5 to 30 min. When specimen was austenitixed for 130 sec at $925\;^{\circ}C$ and for 230 sec at $875\;^{\circ}C$, pearlite was transformed into austenite. Bainite around graphite was found at $925^{\circ}C$ for 170 sec. Bainite in grain boundary of ferrite was happened at $875^{\circ}C$ for 350 sec. During the austempering process, acicular bainite was precipitated at $300^{\circ}C$ and lath bainite was precipitated at $400^{\circ}C$. Increment in manganese content restrained bainitic transformation. Retained austenie was of little quantity.