MICROSTRUCTURE OF COMBINATION CLASP JOINTS IN REMOVABLE PARTIAL DENTURE

가철성(可撤性) 국부의치(局部義齒)에서 연합(聯合) Clasp 연결부위(連結部位)의 미세구조(微細構造)

To evaluate the microstructure of various combination clasp joint in removable partial denture, the auther selected framework alloys (Type IV gold alloy, Dentaurium, Ticonium 100) and wrought wires (gold alloy, Ticonium) for this study. Twelve series of combination joints were made by investment soldering technic and wrought wire embedded casting technic. All specimens were cut cross-sectionally and longitudinally, then examined with metallurgical microscope. The results were as follows; Some diffusion was observed in the properly constructed combination clasp joints. In soldered joints, empolying precious alloys were more favorable than non-precious alloys. In castion joints, assemblage of same alloy between framework and wrought wire was superior to other groups. Some impurities were observed in both joints by technical problems.

매몰(埋沒) 납착법과 가공선(加工線) 봉매(封埋) 주조법(鑄造法)에 의해 국부의치(局部義齒)의 금속(金屬)과 가공선(加工線)을 각각(各各) 귀금속(貴金屬) 및 비귀금속(非貴金屬)으로 제작(製作)하였을 때 연합(聯合) clasp 연결부(連結部)의 미세구조(微細構造)를 금속(金屬) 현미경(顯微鏡)으로 관찰(觀察)하여 다음과 같은 결과(結果)를 얻었다. 납착 및 주조시편(鑄造試片) 공(共)히 연결부위(連結部位)의 미세조직(微細組織)은 확산(擴散)에 의한 다소(多少)의 결정립계(結晶粒界)의 변화(變化)를 관찰(觀察)할 수 있었다. 납착시편에서는 비귀금속(非貴金屬)보다 귀금속(貴金屬) 사용(使用)시 양호(良好)한 결합양상(結合樣相)을 나타내었다. 납착시편에서는 귀금속(貴金屬) 및 비귀금속(非貴金屬) 차이(差異)보다는 같은 계통(系統)의 금속(金屬)을 사용(使用)함으로서 보다 양호(良好)한 결합양상(結合樣相)을 나타내었다. 주조시편(鑄造試片)과 납착시편 모두에서 시편제작(試片製作)의 기술적(技術的)인 방법(方法)에 의해 다소(多少)의 기공(氣孔) 및 산화물(酸化物) 형성(形成) 등(等)과 같은 오염(汚染)된 계면부(界面部)가 나타났다.