Electron Dose Measurement with Polycarbonate Film Dosimeter

Dosimetrical properties of polycarbonate film for high-level dosimetry of electrons have been examined. Polycartonate film of 0.1mm in thickness was chosen for this purpose. It can cover the dose range of 1.0-130 Mrad and the measurable range can be extended up to 200 Mrad by using calibration curve. The measurement error was within 3.5%. The radiation induced optical density at 330nm shows rapid initial fading of 7-l3n for one day after irradiation at room temperature and subsequent fading rate is very small, about 0.6% per day. The fading depends on the absorbed dose, storage temperature, and wavelengths. The effects of storage time and temperature during and after irradiation of this film are presented. For practical dosimetry, it is necessary to stabilize the induced optical density by storing the irradiated film for a day or by heat treatment at 10$0^{\circ}C$ for an hour.

고준위 전자선량을 측정하기 위하여 두께 0.1mm인 polycarbonate 필름을 선정하여 선량계 특성을 조사하였다. 선량범위는 1.0-130Mrad이며 도정곡선을 이용하여 200Mrad까지도 측정할 수 있었고 측정요차는 3.5% 이내였다. 330nm데서 측정한 농도는 실온에서는 조사후 1일 동안에 약 7-13% 감소하였으며 그 후의 감소율은 매우 적어 약 0.6%/일 였다. 조사후의 농도변화는 흡수선량, 보존온도 및 파장에 따라 상이하였기 때문에 조사후 경과시간 및 보존온도와 조사시의 온도에 관한 효과를 검토하였다. 이 선량계를 사용할때에는 농도 변화의 오차를 줄이기 위해서는 1일후에 농도를 측정하거나 혹은 10$0^{\circ}C$에서 1시간 열 처리가 필요하였다.