Abstract
Hafnium Oxide (HfOx) has been attracted as a promising gate dielectric for replacing SiO2 in gate stack applications. In this paper, Metal-Oxide-Semiconductor (MOS) capacitor with solution processed HfO2 high-k material as a dielectric were fabricated. The solvent using $HfOCl2{\cdot}8H2O$ dissolve in 2-Methoxy ethanol was prepared at 0.3M. The HfOx layers were deposited on p-type silicon substrate by spin-coating at $250^{\circ}C$ for 5 minutes on a hot plate and repeated the same cycle for 5 times, followed by annealing process at 350, 450 and $550^{\circ}C$ for 2 hours. When the annealing temperature was increased from 350 to $550^{\circ}C$, capacitance value was increased from 337 to 367 pF. That was resulted from the higher temperature of HfOx which have more crystallization phase, therefore dielectric constant (k) was increased from 11 to 12. It leads to the formation of dense HfOx film and improve the ability of the insulator layer. We confirm that HfOx layer have a good performance for dielectric layer in MOS capacitors.