0.04% Gd-이상 스테인레스 강의 부식 및 마모성에 대한 집합조직 효과

Effect of Texture on the Corrosion and Wear Behaviors of 0.04% Gd-Duplex Stainless Steels

0.04% Gd-duplex stainless steels (Gd-DSTSs) for neutron absorbing materials were inert arc-melted and poured into a Y-shape block with the size of $100{\times}100{\times}20[mm]$. The Gd-DSTS was hot rolled at $1200^{\circ}C$ followed by cold rolling to have 33% reduction. The average grain sizes of the rolling (RD), transverse (TD) and short transverse (ST) directions were 6, 7, $11{\mu}m$, respectively. The micro-hardnesses of the RD, TD and ST directions were 258.5, 292.3, 314.7 $H_V$, respectively. Corrosion potential and corrosion rate of the cold rolled Gd-duplex stainless steel in aerated artificial sea water and 0.1M $H_2SO_4$ solution were $0.2216V_{SHE}$, $0.0106A/cm^2$, $-0.0825V_{SHE}$, $0.0168A/cm^2$ for RD, $0.2210V_{SHE}$, $0.0077A/cm^2$, $0.0817V_{SHE}$, $0.0092A/cm^2$ for TD, $0.1056V_{SHE}$, $0.0059A/cm^2$, $0.0475V_{SHE}$, $0.0069A/cm^2$ for ST, respectively. The corrosion behavior depended on the texture, which were due to mainly grain boundary and minorly crystallographic texture. Friction coefficient and wear resistance were 2.07 and 0.48 mm, respectively.