Spalling Properties of 80MPa High Strength Concrete with Fiber

복합섬유(PP,NY)를 혼입한 설계강도 80MPa 3성분계 고강도콘크리트의 폭렬특성

In this study, the fire resistance test was carried out with a parameter such as fiber(PP+NY) mixed ratio on high strength concrete with 80MPa, and the spalling resistance property was evaluated. Concrete material test was carried out with a parameter such as fiber(PP+NY) mixed ratio(0%, 0.05%, 0.1%, 0.2%) of high strength concrete with 80MPa. Although the flowability and the strength capacity were delicately decreased with a increase of fiber mixed ratio, they satisfied the target limits. As the spalling resistance property after the fire resistance test of 3 hours, the spalling was partly shown on the high strength concrete with fiber(PP+NY) mixed ratio of 0% but, wasn't shown on the high strength concrete with fiber(PP+NY) mixed ratio of 0.05% ~ 0.2%.