Property change of organic light-emitting diodes due to an ITO surface reformation

ITO 표면 개질에 의한 유기 발광 소자의 특성 변화

We have studied a property change of organic light-emitting diodes (OLED) due to an indium tin oxide (ITO) surface reformation. The characteristics of OLED were improved by oxygen plasma processing of an ITO in this work. ITO is widely used as a transparent electrode in light-emitting devices, and the OLED device performance is sensitive to the surface properties of the ITO. The OLED devices with the structure of ITO/TPD(50nm)/$Alq_3$(70nm)/LiF(0.5nm)/Al(100nm) were fabricated, and the surface properties of ITO were investigated by using various characterization techniques. The oxygen plasma process of an ITO was processed by using RF power of 125W and oxygen partial pressure of $2\times10^{-2}$ Torr. The oxygen plasma processing of an ITO processed for 0/1/2/3/4min. Current-voltage-luminance characteristics of the devices show that turn-on voltage is 4V for 2min device and the luminance reaches about 27,000cd/$m^2$ for 4min device. The current efficiency shows that 3min device becomes saturated to be about 8cd/ A. They show that emission was from the $Alq_3$ layer, because the peak wavelength is about 525nm. View angle-dependent emission spectra show that the emission intensity decreases as the angle increases.