• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.314-315
• /
• 2008

We have studied a property change of organic light-emitting diodes (OLED)s due to a surface reformation of indium-tin-oxide(ITO) substrate. An ITO is widely used as a transparent electrode in light-emitting diodes, and the OLEDs device performance is sensitive to the surface properties of the ITO. The ITO surface reformation could reduce the Schottky barrier at the ITO/organic interface and increase the adhesion of the organic layer onto the electrode. We have studied the characteristics of OLEDs with a treatment by a wet processing of the ITO substrate. The self-assembled monolayer(SAM) was used for wet processing. The characteristics of OLEDs were improved by SAM treatment of an ITO in this work. The OLEDs with a structure of ITO/TPD(50nm)/$Alq_3$(70nm)/LiF(0.5nm)/Al(100nm) were fabricated, and the surface properties of ITO were investigated by using seneral characterization techniques. Self-assembled monolayer introduced at the anode/organic interface gave an improvement in turn-on voltage, luminance and external quantum efficiency compared to the device without the SAM layer. SAM-treatment time of the ITO substrate was made to be 0/10/15/20/25min. The current efficiency of the device with 15min. treated SAM layer was increased by 3 times and the external quantum efficiency by 2.6 times.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.411-412
• /
• 2008

We have studied a property change of organic light-emitting diodes (OLED) due to an indium tin oxide (ITO) surface reformation. The characteristics of OLED were improved by oxygen plasma processing of an ITO in this work. ITO is widely used as a transparent electrode in light-emitting devices, and the OLED device performance is sensitive to the surface properties of the ITO. The OLED devices with the structure of ITO/TPD(50nm)/$Alq_3$(70nm)/LiF(0.5nm)/Al(100nm) were fabricated, and the surface properties of ITO were investigated by using various characterization techniques. The oxygen plasma process of an ITO was processed by using RF power of 125W and oxygen partial pressure of $2\times10^{-2}$ Torr. The oxygen plasma processing of an ITO processed for 0/1/2/3/4min. Current-voltage-luminance characteristics of the devices show that turn-on voltage is 4V for 2min device and the luminance reaches about 27,000cd/$m^2$ for 4min device. The current efficiency shows that 3min device becomes saturated to be about 8cd/ A. They show that emission was from the $Alq_3$ layer, because the peak wavelength is about 525nm. View angle-dependent emission spectra show that the emission intensity decreases as the angle increases.