The Corrosion Behavior of Rebar Embedded in Concrete With Chloride.

염화물 혼입에 따른 철근의 부식 거동

As embedded reinforcing suffer from corrosion process, the bond strength and stiffness are reduced, and the structure proceed, eventually, to the deterioration of the concrete, shortening the service life of concrete structures rapidly. In order to deal with these problems, a multitude of researches have been carried out up to this date to evaluate the bond characteristics of RC members, i.e. by artificially inducing rapid corrosion of the reinforcing bar. These artificial corrosion methods, however, could not represent the real condition, resulting in the possibility of overestimation for the RC members in real situation. Accordingly, the purpose of this paper is to investigate the difference in the bond characteristics for RC members corroded by different corrosion methods (artificial rapid method, natural method). For the case of natural corrosion, the brittle failure was observedeven for the case of the area ofcorrosion of 50%. And, the bond strength decreased by about 10% or more for the caseofspecimens with the area of corrosion of 80% or above. Especially, the deterioration of concrete starts at the state of low corrosion level for the case of natural corrosion. Thus, the safety of RC members must be assessed and evaluated more carefully for the naturally corroded members than for the RC concrete members corroded rapidly by artificial method.

매립된 철근의 부식이 진행될 경우, 부착강도 및 강성이 감소되며, 구조물의 열화가 발생하여 사용 수명이 단축된다. 이러한 문제를 해결하기 위하여 RC 부재의 부착특성에 대한 평가가 인위적으로 철근을 빠르게 부식시키는 방법을 통하여 지금까지 연구되어왔다. 그러나, 이러한 인위적인 부식방법은 실제 부식 상황과 일치하지 않으며, 결과적으로 실제 상황에서의 RC 부재에 대한 부식 가능성을 과대평가할 수 있다. 따라서, 본 연구는 인위적인 방법과 자연적인 방법에 의해 RC 부재를 부식시킴으로써 부착 강성의 차이를 평가하고자 하였다. 자연적인 부식의 경우, 부식면적 50%에서 취성파괴가 발생했으며, 부식면적 80%이상에서는 부착강도가 약 10%이상 감소하였다. 특히, 자연적 부식의 경우 낮은 부식수준에서 콘크리트의 열화가 발생하였다. 따라서 향후 부식에 따른 부재의 성능저하를 평가하고자 할 경우에는 인위적으로 부식시킨 시험체로부터 평가하는 것은 곤란하며 반드시 자연적으로 부식시킨 시험체를 사용하여 성능을 평가해야 한다고 판단된다.