This study analyzed the basic characteristics of concretes to develop 3 ingredients high performance concrete that displaced BS and FA, and the results are as follows. As part of fresh concrete characteristics, the flow was shown more increase than OPC with increase in admixture material displacement rate, and air amount tended to decrease with increase in admixture displacement rate. As hardened concrete characteristics, compressive strength decreased below OPC at early age with increase in BS and FA displacement rate, however at age 28 days, it was similar to OPC or increased above that. Particularly, at B30F15 with age 28 days, its compressive strength was about 15% higher than OPC

본 연구에서는 BS와 FA를 치환한 3성분계 고성능 콘크리트의 개발을 위해 기초적 특성을 분석하였는데, 그 결과를 요약하면 다음과 같다. 굳지않은 콘크리트 특성으로, 유동성은 혼화재 치환율이 증가할수록 OPC보다 증가하는 것으로 나타났고, 공기량은 전반적으로 혼화재 치환율이 증가할수록 감소하는 경향을 나타내었다. 경화 콘크리트 특성으로, 압축강도는 BS와 FA의 치환율이 증가할수록 초기재령에서는 OPC보다 저하하는 것으로 나타났으나, 재령 28일에서는 OPC과 유사하거나 그 이상으로 증가하는 것으로 나타났다. 특히 B30F15일때 재령 28일에서 OPC보다 약 15% 정도 높은 최대 압축강도 값을 발휘하였다.