Effect of Hydration Heat and Drying Shrinkage of Mass Concrete Using Hwangtoh Binder

황토결합재를 이용한 매스콘크리트의 수화열과 건조수축 효과

In this paper, the applicability of hwangtoh, as an alternative of cement paste, is investigated for the solution of internal heat and shrinkage caused by the hydration of cement paste. Several small-sized specimens of hwangtoh and ordinary portland concrete(OPC) were compared as to compressive strength, heat of hydration, and shrinkage strain. Moreover, the applicability of mass structure was reviewed through the test of large-size specimens. The 28-day compressive strength of hwangtoh concrete(HBC), ranged 18 to 33 Mpa, can reach that of ordinary portland concrete. Not only the maximin internal temperature of HBC was read about 1/4 of OPC as it is cured, but also its drying shrinkage decreased as lower as 50% of OPC starting from 60 days. Therefore, hwangtoh binder is more favorable than cement one in the view of hydration heat and shrinkage under the construction of mass structures.

본 연구는 황토결합재로 시멘트를 대체함으로써 시멘트의 수화 반응 등에 의한 콘크리트 내부발열과 건조수축 문제의 해결 가능성을 연구하였다. 소형모형에서 HBC는 28일 압축강도가 18${\sim}$33MPa으로 보통강도 콘크리트의 강도를 발현할 수 있으면서, OPC에 비해 양생시 내부의 최고온도가 1/4 정도로 낮게 나타나고 건조수축 역시 HBC는 OPC에 비하여 50% 감소하였다. 대형시편에서도 HBC는 낮은 수화열로 인해 내부온도가 OPC에 비해 50% 낮게 나타났으며 건조수축 역시 60일 기점으로 OPC의 50% 정도의 수축률을 나타났다. 따라서 황토 결합재를 이용하여 매스 구조물을 제작하면 시멘트에 비하여 수화열과 건조수축의 문제를 해결하는데 상대적으로 유리할 것으로 사료된다.