An Experimental Study on Corrosion Resistance of Cracked Concrete

균열 콘크리트에서의 부식저항성에 관한 실험적 연구

  • 송하원 (연세대학교 사회환경시스템공학부) ;
  • 이창홍 (연세대학교 사회환경시스템공학부) ;
  • 안기용 (연세대학교 사회환경시스템공학부) ;
  • 이근주 (연세대학교 사회환경시스템공학부)
  • Published : 2008.04.24
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, corrosion resistance of steel in cracked-reinforced concrete was performed according to experimental method. Mixed design is OPC, 30% PFA, 60% GGBS and 10% SF, respectively. Moreover, corrosion resistance test was measured using ultra testing machine for 0.3mm crack induction. The corrosion resistance of blended concrete shows the results following OPC > 10%SF > 30% PFA > 60% GGBS after 60days curing. In case of mass loss test, embedded reinforcement in OPC concrete surveyed the minimum corrosion and appeared better corrosion resistance than blended concrete. As a result, corrosion resistance of sound concrete is higher than cracked concrete. Moreover, corrosion resistance of binary concrete is lower than OPC.

본 연구에서는 균열 철근콘크리트에서의 철근의 부식 저항성 평가를 실험적 방법에 의해 수행하였다. 실험 배합으로서 보통포틀랜드시멘트(OPC), 30% 치환률의 플라이애쉬(30% PFA), 60% 치환률의 고로슬래그미분말(60% GGBS), 10% 치환률의 실리카퓸(10% SF)이 적용된 콘크리트보를 사용하였으며, 부식저항성 실험은 만능시험기를 사용하여 0.3mm의 균열을 도입하여 측정하였다. 실험결과, 혼합콘크리트 균열 철근보의 60일 양생 후의 부식저항성 순서는 OPC > 10%SF > 30% PFA > 60% GGBS로 나타남을 확인하였다. 또한, 무게감량법에 의한 부식량 측정결과도 OPC의 경우가 가장 높은 부식저항성을 가지면서 최소의 부식을 발생시키고 있음을 확인하였다. 실험결과로써 건전부 콘크리트보에서의 부식저항성이 균열부 콘크리트에서의 부식저항성보다 높게 나타나고 있음을 확인할 수 있었고, 또한, 이성분계 콘크리트보다 OPC 콘크리트가 부식 저항이 더욱 높음을 확인하였다.