An Experimental Study on the Properties of Concrete with Regional Fine Aggregate Properties and Modulation of Fine Aggregate Ratio

지역별 잔골재특성 및 잔골재율 조정에 의한 콘크리트 특성에 관한 실험적 연구

This study investigated the best condition when mixed sand with a river and crushed sand was used though the experiment for the properties of the concrete corresponding to the control of fine aggregate ratio to apply the mixed sand and properties of the fine aggregate at the ready-mixed concrete factory on Yeongnam and Honam. The physical properties of Yeongnam and Honam is satisfied with KS F 2526 and KS F 2527 except fineness modulus and passing amount of 8mm sieve. And, the mixed sand above two types which were incongruent to use individually was being used at each factory, and it was managed in accordance with KS. The flowabillity of the mixture proportion of concrete which was estimated by method of unit volume weight according to the fine aggregate ratio at each factory on Yeongnam and Honam was higher than existing mixture proportion. It was analyzed that the residual water due to decline of the surface area caused by reducing fine aggregate ratio was increased relatively. Accordingly, it was considered that the effect on the economic mixture proportion and improvement of durability might be possible.

본 연구는 영, 호남 지역의 레미콘 공장에서 현재 사용하고 있는 잔골재의 특성을 분석하고, 혼합사용 시 잔골재율 조정에 따른 콘크리트의 특성실험을 통하여 혼합사용 시 최적조건을 분석한 것으로 그 결과를 요약하면 다음과 같다. 영, 호남에서 사용하는 골재 종류별 물성은 조립률 및 0.08mm체 통과량을 제외하고 모두 KS F 2526 및 KS F 2527의 규정에 적합한 것으로 나타났는데, 각 공장에서는 단독사용이 부적합한 골재를 2종 이상 적절한 비율로 혼합사용하고, KS규정에 적합하게 품질을 관리하고 있었다. 영, 호남 각 공장에서 단위용적질량법에 의해 산출한 잔골재율로 조정한 콘크리트의 배합은 기존의 출하배합보다 높은 유동성을 보이는 것으로 나타났는데, 이는 잔골재율 약 2% 저감에 따라 잔골재의 표면적 감소 및 공극감소에 따른 시멘트 페이스트의 유동성에 미치는 잉여수량의 상대적 증가에 기인한 것으로 분석된다. 따라서 최적 잔골재율을 적용함으로써 단위수량 감소로 인한 경제적인 콘크리트 배합과 콘크리트의 내구성을 증진시키는 효과가 있을 것이라 사료된다.