Abstract
In this study, Assessment of bond property of HSC with the rate of Blust-furnace(0, 12, and 25 percent by weight cement) and Evaluation of the relationship of the compressive strength coefficient (${\beta}$) between compressive strength with 40${\sim}$120MPa were performed. Design and Test of Bond specimens were carried out based on the ASTM C-234. Test results are follows, most specimens showed that the splitting failure in all specimens, except for B-40 series which showed that the pull-out failure. For the B-40 Series, the relation of compressive strength versus bond stress has well converged that of the proposed equation with the variation(${\beta}$=2/3) in UCB/E.E.R.C-83. The crack strength of concrete in splitting was proportioned to the compressive strength of concrete, and was the highest on the contents of blast furnace slag to 12 percent by weight of cement in each series, except for B-60 series. In the relation of admixture replacement rate versus maximum bond stress, The maximum bond stress was the highest in 12 percent by weight of cement according to less than 40MPa, and was the highest in 25 percent by weight of cement according to 80MPa.
본 연구에서는 설계강도 40${\sim}$120MPa인 3성분계 콘크리트를 대상으로 부착실험을 수행하여 혼화재 (고로슬래그)대체율과 부착파괴강도와의 관계와 콘크리트 강도와 철근의 부착응력 변화관계를 평가하였다. 부착시험체의 제작과 실험은 ASTM C-234에 준하여 수행하였으며, 혼화재인 고로슬래그 대체율이 각 시험체에 대하여 각각 0, 12, 25%이고 콘크리트 압축강도가 40${\sim}$100MPa인 경우에 대한 철근-콘크리트의 부착성능을 조사 하였다. 부착실험 결과, 압축강도가 40MPa 시험체(B-40계열)만 뽑힘파괴가 발생하였고, 나머지 시험체 (B-60${\sim}$B-120)에서 쪼갬파괴가 발생하였다. B-40 계열의 경우, UCB/EERC-83에서 제시된 부착강도 평가식의 영향 변수(${\beta}$)가 2/3 일 때 콘크리트의 압축강도의 변화에 따른 철근의 부착응력을 수렴하고 있음을 알 수 있었다. 쪼갬이 발생한 시점의 균열강도는 콘크리트 압축강도와 비례하였으며, B-60 시리즈를 제외한 각각의 압축강도 시리즈에서 고로슬래그 시멘트 대체율이 12% 이었을 경우, 그 값이 가장 크게 나타났다. 최대부착응력은 압축강도 40MPa이하일 경우 그 대체율이 12%일 때 가장 크며, 압축강도 80MPa일 경우 그 대체율이 25%일 때 가장 큰 것으로 나타났다.