A Study on the Development of a Dry PFB Method with High Fire Resistance

건식화 P0SCO E&C Fire Board (PFB)공법 개발에 관한 연구

The present study was to develop a dry PFB method similar to the existing gypsum board construction method in order to apply the existing wet PFB method that uses fire.resistant adhesive. It was found that the existing wet method can produce concrete compressive strength of 80MPa and fire resistance of 3 hours with 30mm PF boards. The goal of development in this study was fire resistance of 3 hours through dry construction of 15mm fire.resistant boards.According to the results of fire resistance test, when the dry PF method was applied, the temperature of the main reinforcing bar was 116$^{\circ}$C in 15mm, 103.8$^{\circ}$C in 20mm, and 94$^{\circ}$C in 25mm, and these results satisfied the current standards for fire resistance control presented by the Ministry of Land, Transport and Maritime Affairs. When a 3.hour fire resistance test was performed and the external properties of the specimen were examined, the outermost gypsum board hardly remained and internal PF board maintained its form without thermal strain.

국내 초고층 프로젝트의 증가에 따라 필연적으로 고강도 콘크리트의 사용이 증가되고 있다. 콘크리트의 강도가 증가됨에 따라 화재시 단면결손을 유발하는 폭렬의 경향성이 커지고, 콘크리트부재 내부의 온도를 현저하게 증가시키며 심각한 구조적 손상을 유발할 수 있다는 문제점이 대두되었고, 정부에서도 2008년 7월부터 고강도 콘크리트의 내화성능 관리기준을 시행하고 있다. 이에 국내 각 건설사들은50MPa 이상의 고강도 콘크리트에 대하여 폭렬방지 대책을 수립 중에 있다. 본 연구소에서는 신축공사 및 리모델링공사에도 적용이 가능한 고강도 콘크리트 폭렬방지 공법인 PFB (Posco E&C Fire Board) 공법을 개발하여 지속적인 공법 개선에 노력하고 있다. 본 연구는 고강도 콘크리트 폭렬방지 대책으로 개발한 PFB 공법 개발에 대한 일반사항, 현재 건식화 공법 개발 및 당사 PJT적용 현황에 대한 내용을 기술하고자 한다.