In this paper, insulating effect and strength development of concrete under low temperature are reported varying curing sheets. According to test results, in temperature -5$^{\circ}$C concrete subject to exposure and air cap condition, result in a frost damage at early age by a fall of below zero temperature. Mean while, the combination of PE film and non-woven fabric maintained around 3 $^{\circ}$C within first 24 hours since placement. For double bubble sheets, concrete temperature maintained above 7$^{\circ}$C due to its excellent heat insulating capability. As a result of core strength test, strength of specimens cured with viny + non-woven fabric and double bubble sheets had higher strength than strength of other specimens due to good heat insulation effect at early age.
본 연구에서는 저온 환경에서 단열양생시트 변화에 따른 콘크리트의 온도이력 및 강도특성을 검토하였다. 실험결과 -5$^{\circ}$C에서 노출과 air cap포장지의 경우 초기 24시간 이내로 콘크리트의 온도가 영하의 온도로 저하되어 초기동해가 발생되었다. 반면, 비닐+부직포의 경우 초기 24시간이내의 최저온도가 약 3$^{\circ}$C로 영상의 온도를 유지하였고 이중버블시트의 경우 약 7$^{\circ}$C로 나타나 양호한 단열 보온성능을 나타내었다. 코어압축강도를 측정한 결과 비닐+부직포와 이중버블시트로 양생한 시험체의 압축강도가 양생초기의 우수한 단열효과로 인해 다른 시험체의 압축강도보다 높게 나타났다.