Study on Performance of Lithium-Silicate Permeation and Changing Prosity Structure according to Water Content

수분의 함수율에 따른 공극구조의 변화와 리튬실리케이트의 침투성

Pores can become factors of reducing the capacity of concrete by being path of degradation factors and moisture can fill up pores inside of concrete, so evaluating the effect of unidirectional permeability due to moisture on pore structure of concrete structure is very important. Therefore, the change of pore structure in cases of 0%, 40%, 60%, 80% and 90% humidity being maintained on test specimens and in case of Lithium Silicate, which is chemical compound, being coated were evaluated. As a result, the condensation due to moisture could be confirmed since unidirectional permeability was decreased and the density of Pore Structure was improved as the percentage of water content was being increased. And, solution-type Lithium Silicate fills up pores of sizes around 1$\mu$m in the condition of carrying water and improves the density but the range of capacity improvement due to osmosis will be limited according to functional conditions.

공극은 열화인자의 이동경로가 되어 콘크리트의 성능을 저하시키는 요인으로 작용할 수 있으며 수분은 콘크리트 내부의 공극을 충전시킬 수 있기에 수분에 의한 투기성이 시멘트경화체의 공극구조에 미치는 영향을 평가하는 것은 중요하다. 이에, 본 연구에서는 공극구조와 투기성에 대하여 0%, 40%, 60%, 80%, 90%의 습도를 유지시킨 시험체와 화학조성물인 리튬실리케이트를 도포시켰을 경우의 공극구조 변화를 평가하였다. 그 결과, 함수율이 증가할수록 투기성은 저하되고 공극구조의 밀실성이 향상되어 수분에 의한 응축현상을 확인할 수 있었다. 그리고 수용액 상태의 리튬실리케이트는 수분을 함유하고 있는 상태에서 1$\mu$m 전, 후의 공극을 충전시켜 밀실성을 향상시키나함수조건에 따라 침투성에 의한 성능향상 범위가 제한적일 것으로 판단된다.