High Temperature Properties of Alumino Silicate Fire Protection Materials Using Fly ash

플라이애쉬 활용 Alumino silicate계 내화마감재의 고온특성

HSC(High Strength Concrete) have superior properties well as improvement in durability compared with normal strength concrete. In spite of durability of HSC, explosive spalling of concrete is serious problem in structure safety. Therefore, Solving methods are required to control the explosive spalling. The properties of concrete are affected by changes of temperatures. Compressive strength and elasticity modulus were degraded depending on a rise of temperatures. Also, change in microstructure and dehydration of concrete subjected to high temperatures. This paper is concerned with change in microstructure and dehydration of the alumino silicate fire protection materials at high temperatures. The testing methods of fire protection materials in high temperature properties are make use of SEM, TG-DSC and XRD. From the experimental test results, influence of high temperatures on microstructure of alumino-silicate fire protection material was identified, including chemical dehydration of C-S-H and CH. The chemical dehydration of CH under various temperatures from to 450 to 600$^{\circ}$C has been measured using the TG-DSC. However, developed alumino silicate fire protection materials showed good stability in high Temperatures. Thus, the results indicate that it is possible to fireproof panels, fire protection of materials.

고강도콘크리트의 화재시의 내화성능 확보와 관련한 대책 및 이에 관한 다수의 연구가 진행되고 있는데 이 중, 고강도콘크리트 자체의 온도상승을 저감하기 위한 방편으로 내화성 마감재의 적용이 검토되고 있다. 일반적으로 시멘트계 재료는 C-S-H, 및 CH가 단계적으로 열 분해되며 압축강도는 저하하게 된다. 내화성능을 발휘하기 위해 고온에서 강도감소가 작고 안정적인 고온특성을 보인다면 보다 효과적으로 성능 발현이 가능하다. 본 연구는 효과적인 내화성능의 발현을 위한 내화성 마감재 개발을 위한 기초연구로 내화성능이 우수하다고 알려진 알루미노 실리케이트계 재료를 내화성 마감에 적용하기 위해 고온특성에 대해 검토하였다.