An Experimental Study on the Improvement of Early Strength and Chloride Attack Resistance for Marine Concrete

해양용콘크리트의 초기강도 및 내염해 저항성 향상에 관한 실험적 연구

The structure which is located in special surroundings like ocean-environment is physically and chemically eroded by seawater or salt damage, and then concrete-structure becomes deteriorated by iron corrosion and swelling pressure which leads to remarkably decline durability due to cracks and exploitation. As a measure against salt damage, it is actively being examined to use the blended cement that controls salt damage and fix chloride in the process of hydration. In this study, therefore, to examine the property of marine concrete added admixture, marine concrete is manufactured by adding high-strength admixture(omega2000) by 0, 5, 10, and 15% to low heat-blended cement. Then it shows that the compressive strength of manufactured marine cement tends to increase and chloride penetration resistance improves.

해양환경과 같이 특수한 환경에 위치한 구조물은 해수 및 염해 등에 의해 물리적 화학적 침식을받아 철근부식과 그 팽창압으로 인해 콘크리트 구조물의 성능저하가 가속화되고 있으며, 이러한 성능저하로 인해 콘크리트 구조물은 균열 박리되어 내구성이 현저히 저하된다. 이러한 염해대책으로는 염해침투를 억제하는 혼합시멘트를 사용하거나, 수화과정에서 염화물을 화학적으로 고정화 시키는 등의연구가 활발히 진행되고 있다. 따라서 본 연구에서는 고강도 혼합재가 첨가된 해양콘크리트의 특성을 검토하기 위하여 저발열 혼합시멘트에 고강도 혼합재(오메가2000)를 0, 5, 10, 15% 치환 첨가하여 해양콘크리트를 제조하였다. 제조한 해양콘크리트의 재령별 압축강도는 증가하는 경향을 나타내었으며, 재령에 따른 염소이온 침투저항성은 향상되는 것으로 나타났다.