A Study on the Autogenous Shrinkage Control of Ultra.High. Strength Concrete -Focused on physical properties and length variation-

초고강도 콘크리트의 자기수축제어에 관한 연구 -물리적 특성과 길이변화율을 중심으로-

As super.high.strength concrete uses a large amount of binder, there is an autogenous shrinkage strain larger than dry shrinkage and it degrades the quality of structures. Thus, we need a technology to minimize the shrinkage strain of super.high.strength concrete. Accordingly, the present study prepared super.high strength concrete with design strength of over 80MPa and, using an embedded gauge, measured the shrinkage strain of free shrinkage specimens for super.high.strength concrete containing expansion agent. According to the results of this study, the expansion rate of concrete increased in the early stage due to the admixture of expansion agent, but the shrinkage rate went down with the lapse of time. The effect of the admixture of expansion agent on compressive strength appeared insignificant. Further research shall be made on different kinds of expansion agents and various mixture ratios for basic analysis to reduce autogenous shrinkage of super.high.strength concrete.

초고강도 콘크리트는 결합재의 다량 사용에 따라 건조수축보다 큰 자기수축 변형이 나타나며 이는 구조물의 품질을 저해하는 요인으로 작용하여 초고강도 콘크리트의 수축변형을 최소화시키기 위한 기술이 필요하다. 이에 본 연구에서는 설계기준강도 100MPa 이상을 갖는 초고강도 콘크리트를 제조하고 팽창제를 혼입한 초고강도 콘크리트에 대하여 자유수축시험체로 매립형게이지를 통한 수축변형을 측정하였다. 그 결과 팽창제의 혼입으로 초기상태의 콘크리트는 팽창율이 증가하나 장기적 측면에서의 수축율이 둔화되는 것으로 나타났으며, 이를 통한 팽창제를 통하여 수축저감에 관한 효과가 기대된다. 아울러팽창제의 혼입에 따른 압축강도에 미치는 영향은 미미한 것으로 나타났다.