Fundamental Properties of the Concrete Incorporating Coarse Particle Cement and Fly Ash

조립시멘트와 플라이애시를 조합 사용한 콘크리트의 기초적 특성

This study analyzed is to investigate the effect of the combined use of fly ash and coarse particle cement(RCC) collected in particle classification method during ordinary portland cement(OPC) on the fundamental properties of concrete. Totally 16 batches of the concrete was fabricated vary the contends of FA and RCC. As results of experiment, in the case of flow, the more the contents of RCC, the larger the flow. And the more the contents of FA displacement rate increased, the less the flow. As for simple adiabatic temperature rise due to the RCC and FA contents, it decreased with the increase of them. And particularly in the case of RCC 30% + FA 30%, temperature rise amount, was very low. Compressive strength decreased in proportion to increase of the contents of FA and RCC. And strength ratio of the concrete incorporating FA and RCC for plain concrete at 28 days was 88%${\sim}$98%, which was relatively good results.

본 연구는 보통포틀랜드 시멘트(이하 OPC)의 제조공정 중 입도 분급에 의해 포집된 조립시멘트(역송분, 이하 RCC)와 저발열 혼화재료인 플라이애시(이하 FA)를 조합 치환하여 사용한 콘크리트의 기초적 특성에 대해 검토하고자 하였다. 실험은 W/B 50% 1수준에 대하여 OPC를 100% 사용한 것을Plain으로 하고, RCC를 0, 10, 20, 30%의 4수준, 혼화재로 FA를 0, 10, 20, 30%의 4수준으로 치환하여총 16배치를 계획 하였다. 실험결과로 유동성의 경우는 RCC를 치환하였을 때 증가하였으며, FA의 치환율이 증가 함에 따라 저하하는 경향을 나타냈다. 간이 단열에 의한 온도 상승량은 RCC 및 FA의치환율이 증가할수록 낮아졌고, FA를 조합하여 사용한 경우는 온도 상승을 저하시키는데 보다 효과적인 것을 알 수 있었으며, RCC30, FA30의 경우는 온도저감효과가 가장 뛰어난 것으로 나타났다. 초기강도는 RCC 및 FA의 치환율이 증가 할수록 저하하였고, 28일에서의 Plain에 대한 강도 발현율은RCC 치환율 별 FA10%에서 Plain에 비해 약 88%${\sim}$98%정도로 비교적 우수한 성능을 나타냈다.