Multi-component $ZnO-In_2O_3-SnO_2$ thin films deposited by RF magnetron co-sputtering

Multi-component $ZnO-In_2O_3-SnO_2$ thin films have been prepared by RF magnetron co-sputtering using targets composed of $In_3Sn_4O_{12}$(99.99%) [1] and ZnO(99.99%) at room temperature. $In_3Sn_4O_{12}$ contains less In than commercial ITO, so that it lowers cost. Working pressure was held at 3 mtorr flowing Ar gas 20 sccm and sputtering time was 30 min. RF power ratio [RF1 / (RFI + RF2)] of two guns in sputtering system was varied from 0 to 1. Each RF power was varied $0{\sim}100W$ respectively. The thickness of the films was $350{\sim}650nm$. The composit ion concentrations of the each film were measured with EPMA, AES and XPS. The low resistivity of $1-2\;{\times}\;10^3$ and an average transmittance above 80% in the visible range were attained for the films over a range of ${\delta}\;(0.3\;{\leq}\;{\delta}\;{\leq}\;0.5)$. The films also showed a high chemical stability with time and a good uniformity.