Modulus and Fractural Side Measurement of Semiconductive Shield (Materials) in Power Cable Using the DMA

DMA를 사용한 전력케이블 내 반도전층 재료의 탄성율 및 에너지 손실 측정

To measure modulus and damping of semiconductive materials in power cable, we have investigated the modulus and damping of semiconductive materials showed by changing the content of carbon black. Then they were produced as sheets after pressing for 20 minutes at 180[$^{\circ}C$] with a pressure of 200[$kg/cm^2$]. The content of conduct ive carbon black was the vailable, and their contents were 20, 30 and 40[wt%], respectively. The modulus and $Tan\delta$ experiments were measured by DMA 2980. Ranges of measurement temperature from -50[$^{\circ}C$] to 100[$^{\circ}C$] and measurement frequency is 1[Hz]. The modulus of specimens was increased according to a increment of a carbon black content. And modulus was rapidly decreased at the glass transition temperature. The $Tan\delta$ of specimens was decreased according to a increment of a carbon black content.