Abstract
High temperature deformation behavior of AZ31 Mg alloy was investigated in this study on the basis of a processing map $(\varepsilon\approx0.6)$. To construct a processing map, compression tests were carried out at wide range of temperatures and strain rates $(T=250\~500^{\circ}C,\;\varepsilon=10^{-4}\~100/s)$. Two regions of high deformation efficiency $(\eta)$ were identified as: (1) a dynamic recrystalization (DRX) domain at $250^{\circ}C$ and 1/s and (2) a superplasticity domain at $450^{\circ}C$ and $10^{-4}/s$. Possible deformation mechanisms operating at high temperature were discussed in relation to the activation energy. A two-stage deformation method was found to be effective in enhancing the superplasticity of AZ31 Mg alloy. From the two-stage deformation method, tensile elongation of $1200\%$ was obtained at the superplastic domain.