침전극 곡률반경에 따른 LLDPE/EVA의 교류트리 특성

A Study on the AC Treeing Characteristics with Tip Radius of Needle Electrode in LLDPE/EVA

Polyethylene used as insulating material of power cable is nonpolar and low dielectric loss polymer. But it has defects of tree generation and accumulation of space charge by an applied voltage resulting in the decreased life and performance. To solve these problems, mixed films with LLDPE and EVA that is similar to LLDPE at physical properties in case of low VA contents were made and tested due to the blend ratios of 80:20, 70:30, 60:40 and 50:50[wt%] respectively. We investigated AC electrical treeing characteristics to acquire the best mixture ratio and effect of the tip radius of needle electrode to develop excellent treeproof materials. The degree of crystallity calculated with XRD pattern is higher for pure LLDPE, 50:50 and 70:30. For DSC analysis, it is confirmed that the melting points of mixed specimens are lower than that of pure LLDPE and higher than pure EVA's. The shape of tree propagation showed that pure EVA was electrical tree shape of the branch type, pure LLDPE and blended specimens was able to confirm tree shape of the bush type. As the tip radius go up in the blend ratio 70:30 specimen, the tree inception voltage rise. Probably the reason is the relaxation of electric field in the specimen with bigger tip ratio. As the 6 specimens were applied AC 5[KV],7.5[KV],10[KV] respectively, tree growth length is far shorter in the specimen with blend ratio 70:30, 50:50 than in pure EVA and pure LLDPE specimen. Conclusively, it is confirmed that specimens of which blend ratio are 70:30 and 50:50 are good in electrical tree retardant characteristics, especially, 70:30 has lower dielectric loss than 50:50 and its mixture ratio is the best.