High Temperature Deformation Behavior of Ti-Al Intermetallic Compound - Microstructure Effect

TiAl 금속간 화합물의 미세조직에 따른 고온변형특성

High temperature deformation behavior of a Ti-Al intermetallic compound has been investigated. Specimens with a near gamma and a lamella structures were obtained by performing heat treatment at 1200 and 1330$^{\circ}C$, respectively, for 24 hr and stabilized at 900$^{\circ}C$ for 4 hr followed by air cooling. A series of load relaxation tests has been conducted on these samples at temperatures ranging from 850 to 950$^{\circ}C$ to construct flow curves in the strain rate range from 10$\^$-6//s to 10$\^$-3//s. Strain hardening was observed even at the temperature of 950$^{\circ}C$ in both the near gamma and the lamella structures. Further aging treatment for 12 hr at test temperatures has found to cause no softening in both microstructures.