초록
In recent year, BLT$(Bi_{3.25}La_{0.75}Ti_3O_{12})$ has been one of promising substitute materials at the ferroelectric random access memory applications. We manufactured $(Bi_{3.25}La_{0.75}Ti_3O_{12})$ Target with a ceramic process. The BLT target was sintered at $1100^{\circ}C$ for 4 hours. Using RF magnetron sputtering, a deposited BLT thin films were estimated about ferroelectric property as a functions of post annealing time. The BLT thin films showed a promoted ferroelectric characteristics at the post annealied sample for 30 minutes. This sample exhibited the (117) preferred crystal orientation, current density of $2{\times}10^{-8}A/cm^2$, a remanent polarization of $10{\mu}C/cm^2$ and a coercive field of 62.1 KV/cm respectively.