Abstract
In this study, CT specimen were prepared from Pressure Vessel Steel which was used for pressure vessel plates for room and low temperature service. And we got the following characteristics from fatigue crack growth test carried out in the environment of room and low temperature at $25^{\circ}C$, -3$0^{\circ}C$, -6$0^{\circ}C$, -8$0^{\circ}C$, -10$0^{\circ}C$ and -12$0^{\circ}C$ and in the range of stress ratio of 0.05 and 0.3 by means of opening mode displacement. At the constant street ratio, the threshold stress intensity factor range ΔK$_{th}$ in the early stage of fatigue crack growth(Region I) and stress intensity factor range ΔK in the stable of fatigue crack growth(Region II) was increased in proportion to descend temperature. It assumed that the fatigue resistance characteristics and fracture strength at low temperature is considerable higher than that of room temperature in the early stage and stable of fatigue crack growth region. The straight line slope relation of logarithm do/dN -ΔK in RegionII, that is, the fatigue crack growth exponent m increased with descending temperature at the constant stress ratio. It was assumed that the fatigue crack growth rate do/dN is rapid in proportion to descending temperature in Region IIand the cryogenic-brittleness greatly affect a material with decreasing temperature.e.greatly affect a material with decreasing temperature.