초록
The electrical and physical charateristics of Pt-Co alloy thin films on $Al_2O_3$ substrate, deposited by r.f cosputtering respectively, were analyzed with thickness of thin films ($1700{\sim}10000{\AA}$) and increasing annealing temperature ($800{\sim}1000^{\circ}C$). At input power of Pt : 4.4 W/$cm^2$, Co : 6.91 W/$cm^2$, working vacuum of 10 mTorr and annealing conditions of $1000^{\circ}C$) and 60 min, the resistivity and sheet resistivity of Pt-Co thin films with thickness of $3000{\AA}$ was $15{\mu}{\Omega}{\cdot}cm$ and 0.5 ${\Omega}/{\square}$, respectively. The TCR value of Pt-Co alloy thin films was measured with various thickness of thin films and annealing conditions. The optimum TCR value of 3850 ppm/$^{\circ}C$ in temperature range($200{\sim}400^{\circ}C$) is gained under conditions $3000{\AA}$ of thin films thickness and $1000^{\circ}C$ of annealing temperature. The thermal charateristics of Pt-Co micro heaters were analysed with Pt-Co RTD integrated on the same substrate. In the analysis of characteristics of Pt-Co micro heaters, the Pt-Co micro heaters with thickness of $3000{\AA}$ and annealing temperature of $1000^{\circ}C$ had a good linearity and temperature is up to $468.2^{\circ}C$ with 2.1 watts of the heating power.