A study on the InSb crystal growth and the Zn diffusion

InSb 결정 성장과 Zn 확산에 관한 연구

Binary compound semiconductor InSb crystal which has direct-transition energy gap (0.17 ev) grown by vertical Bridgman method, then the electric-magnetic and optical properties of InSb crystal were surveyed. The growth rate of the crystals was 1mm/hr and the lattice constant $a_\circ$ of the grown crystal was 6.4863$\AA$. The electrical properties were examined by the Hall effect measurement with the van der Pauw method in the temperature range of 70$\sim$300K, magnetic field range of 500$\sim$10000 gauss. The undoped InSb crystal was n-type, the concentration and the electron mobility were 2$\sim$6 ${\times}$ $10^{16}$$\textrm{cm}^{-3}$ and carrier mobility was 6$\sim$2${\times}$$10^{4}$$cm^{2}$/v.sec at 300K, respectively. The carrier mobility was decreased with $T^{-1/2}$ due to the lattice scattering above 100K, and decreased by impurity scattering below100K. The magnetoresistance was increased 190% at 9000 gauss as compared with non-appliced magnetic field and the magnetoresistance was increased with increasing the magnetic field. Also, the Hall voltage was increased with increasing the magnetic field and decreasing the thickness of sample. The optical energy band gap of InSb at room temperature determined using the IR spectrometer was 0.167eV. The diffusion depth of Zn into InSb proportionally increased with the square root of diffusion time and the activation energy for Zn diffusion was 0.67eV. The temperature dependence of diffusion coefficient was $D=4.25{\times}10^{-3}$exp (-0.67/$K_BT$).