• Tribology and Lubricants
• /
• 제14권1호
• /
• pp.1-6
• /
• 1998

An experimental study was performed to discover the tribological behaviors of pure tin and zinc coated 52100 bearing steel. Pure tin coatings ranging from 30 nm to 30,000 nm and pure zinc coatings ranging from 500 nm to 52,000 nm were produced by a thermal evaporation coating method. Experiments using a thrust ball bearing-typed rolling test-rig were performed for the investigations of the effect of coating thickness on the tribological rolling behavior. Results showed that the existence of optimum film thickness which revealed minimum rolling resistance was discovered for tin and zinc coating. The compatibility of coating material to iron showed no significant effect on the rolling resistance behavior. The hardness of coating material revealed significant influence to the rolling resistance behavior.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제26회 추계학술대회
• /
• pp.51-58
• /
• 1997

An experimental study was performed to discover the tribological behaviors of pure tin and zinc coated 52100 bearing steel. Pure tin coatings ranging from 30 nm to 30,000 nm and pure zinc coatings ranging from 500 nm to 52,000 nm were produced by a thermal evaporation coating method. Experiments using a thrust ball bearing-typed rolling test-rig were performed for the investigations of the effect of coating thickness on the tribological rolling behavior. Results showed that the existence of optimum film thickness which revealed minimum rolling resistance was discovered for tin and zinc coating. The compatibility of coating matehal to iron showed no significant effect on the rolling resistance behavior. The hardness of coating material revealed significant influence to the rolling resistance behavior.

• 한국표면공학회지
• /
• 제34권6호
• /
• pp.537-544
• /
• 2001

In the present study, tin-zinc alloys were coated on a cold-rolled steel sheet with variations of electrolyte concentration, additives quantity and current density employing the Hull cell and circulation cell simulator. With an addition of additives of 2m1/L, tin-zinc deposits containing 10 to 40 percent Zn revealed a good surface appearance with weak acidic electrolytes. The organic additives suppressed the Sn deposition rate and thus increased the zinc contents in tin-zinc coating layers. The zinc contents in the tin-zinc coating layers depended almost linearly on the concentrations of metal ions of tin and zinc. Temperature of the electrolyte affected the composition tin-zinc coating layer. However, the concentration of complexants revealed little effectiveness. The surface morphology of tin-zinc coating showed dense tin and zinc phases with fine equiaxed grains with the high current density.

• 한국표면공학회지
• /
• 제32권1호
• /
• pp.31-42
• /
• 1999

The effect was investigated that aluminium in the zinc bath has on the coating adhesion of Hot-rolled Galvanized Iron(HGI) manufactured without pickling process. It is thought that the coating adhesion of HGI manufactured without pickling process is good due to the fact that increasing aluminium content in the zinc bath makes zinc and aluminium diffuse to the cracks or pores in the scale formed through the reduction heat treatment, and Fe-Zn-Al compound with good ductility is formed in the scale layer and plays a role of anchor between zinc coating and substrate. It is possible that HGI with the good coating adhesion was produced without pickling treatment in the zinc bath with more that 3wt% of Al content even at the $550^{\circ}C$ of conventional reduction heating temperature. In creasing the temperature of heating section and aluminium content in the zinc bath prevents the Zn-Fe alloy. The corrosion resistance of HGI manufactured without pickling process is excellent because of the mixed reaction of zinc sacrifice and aluminium passivity film.

• Corrosion Science and Technology
• /
• 제9권3호
• /
• pp.105-108
• /
• 2010

The product specification of the Continuous Hot Dip Galvanizing Line (CGL) changes and varies constantly with different customers' requirements, especially in the zinc coating weight which is from 30 to 150 g/$m^2$ on each side. Since the coating weight of zinc changes often, it is very important to reduce time spent in the transfer of target values changed for low production cost and yield loss. The No.2 CGL in China Steel Corporation (CSC) has improved the control of the air knife which is designed by Siemens VAI. CSC proposed an experiment design which is an $L_9(3^4)$ orthogonal array to find the relations between zinc coating weight and the process parameters, such as the line speed, air pressure, gap of air knife and air knife position. A non-linear regression formula was derived from the experimental results and applied in the mathematical model. A new air knife feedforward control system, which is coupled with the regression formula, the air knife control system and the process computer, is implemented into the line. The practical plant operation results have been presented to show the transfer time is obviously shortened while zinc coating weight target changing and the product rejected ratio caused by zinc coating weight out of specification is significantly reduced from 0.5% to 0.15 %.

• Corrosion Science and Technology
• /
• 제23권3호
• /
• pp.228-234
• /
• 2024

Zinc wiping is a phenomenon used to control zinc-coating thickness on steel substrate during hot dip galvanizing by equipment called air knife. Uniformity of zinc coating weight in length and width profile along with surface quality are most critical quality parameters of galvanized steel. Deviation from tolerance level of coating thickness causes issues like overcoating (excess consumption of costly zinc) or undercoating leading to rejections due to non-compliance of customer requirement. Main contributor of deviation from target coating weight is dynamic change in air knives equipment setup when thickness, width, and type of substrate changes. Additionally, cold coating measurement gauge measure coating weight after solidification but are installed down the line from air knife resulting in delayed feedback. This study presents a coating weight control model (Galvantage) predicting critical air knife parameters air pressure, knife distance from strip and line speed for coating control. A reverse engineering approach is adopted to design a predictive, prescriptive, and descriptive model recommending air knife setups that estimate air knife distance and expected coating weight in real time. Implementation of this model eliminates feedback lag experienced due to location of coating gauge and achieving setup without trial-error by operator.

• Corrosion Science and Technology
• /
• 제15권1호
• /
• pp.1-5
• /
• 2016

Zinc ethyl silicate coatings containing multi walled carbon nanotubes (MWCNTs) were prepared, to which we added spherical and flake shaped zinc particles. The anti-corrosive effects of MWCNTs and zinc shapes on the zinc ethyl silicate coated carbon steel was examined, using electrochemical impedance spectroscopy and corrosion potential measurement. The results of EIS and corrosion potential measurement showed that the zinc ethyl silicate coated with flake shaped zinc particles and MWCNT showed lesser protection to corrosion. These outcomes were in agreement with previous results of corrosion potential and corrosion occurrence.

• 콘크리트학회논문집
• /
• 제26권3호
• /
• pp.299-306
• /
• 2014

콘크리트 구조물의 철근 부식 문제를 해결하기 위하여 코팅철근이 사용된다. 에폭시 코팅 철근에 비해 아연코팅철근의 콘크리트 보의 휨 거동 영향에 대한 자료는 거의 없는 실정이다. 이 연구의 목적은 아연코팅철근이 콘크리트 보의 휨 거동에 미치는 영향을 파악하는 데 있다. 아연코팅철근을 사용한 부재와 일반철근을 사용한 부재의 구조실험을 통하여 휨 거동 특성을 비교하였다. 실험변수로써 철근의 아연코팅 유무, 사용 철근비와 피복 두께를 고려하였다. 아연코팅철근 콘크리트 보의 균열패턴, 균열폭, 처짐 및 변형률 특성을 파악하였다. 아연코팅철근 콘크리트 보의 휨강도는 일반철근 콘크리트 보의 휨강도와 거의 차이가 나지 않는다. 철근표면의 아연코팅은 처짐, 균열폭 비교 결과에도 뚜렷한 영향을 미치지 않는다. 또한, 아연코팅철근 보와 일반철근 보의 하중-변형률 곡선은 비슷한 결과를 나타낸다. 따라서, 전반적으로 아연코팅철근의 사용은 일반철근을 사용할 때에 비해 콘크리트 보의 휨 거동에 악영향을 미치지는 않는 것으로 나타난다.

• Corrosion Science and Technology
• /
• 제9권5호
• /
• pp.175-186
• /
• 2010

The auto industry is demanding more ductile high-strength steel grades to build lighter and stronger car bodies. The hot-dip galvanizing problems of these new steel grades are creating a demand for an improved method to control zinc wettability. The simplest way to improve zinc wettability on industrial hot-dip galvanizing lines is to increase the strip immersion temperature at zinc bath entry for enhancing the aluminothermic reaction. However, this practice increases the reactivity due to overheating the zinc in the snout which induces the formation of brittle Fe-Zn compounds at the strip/coating interface with the formation of higher amounts of dross in the zinc bath and snout contamination. Thus, this simple practice can only be utilized for short production periods of one to two hours without deteriorating coating quality. This problem has been solved by employing a technique that allows the use of a higher and attuned strip immersion temperature at zinc bath entry while still maintaining a constantly low zinc bath temperature. This has been proven to provide the solution for both the improved wettability and a significant reduction in the amounts of dross in the zinc bath.

• Corrosion Science and Technology
• /
• 제18권1호
• /
• pp.24-32
• /
• 2019

The effects of zinc coating and heat treatment on the corrosion resistance of aluminum alloys including A1100 and the modified A3003, used as heat exchanger tube were investigated in this study. The grain size of the heat-treated specimen is larger than that of the specimen without heat treatment, but the grain size did not significantly affect the corrosion behavior. The concentration of zinc was noted at 11.3 ~ 31.4 at.% for the as-received Zn-coated samples and reduced to 1.2 ~ 2.4 at.% after the heat treatment, as measured by the scanning electron microscopy (SEM) with an energy dispersive spectrometer (EDS) on the surface. The concentration of oxygen is 22 ~ 46 at.% for the zinc coated specimens while noted at 7.4 ~ 12.8 at.% for the specimens after the removal of the coating. The corrosion behavior depended largely on the concentrations of zinc, aluminum, and oxygen on the specimen surface, but not on the Mo content. The corrosion potential was high and the corrosion rate was low for a specimen with a low zinc content, a high aluminum content, and a high oxygen content.