• Journal of the Korean Society of Safety
• /
• v.31 no.2
• /
• pp.83-89
• /
• 2016

As the world's industrial development quickens, the highways and regional expressways have been expanding to serve the logistics and transportation needs of people. The burgeoning road construction has led to a growing interest in roadside installations. These must have reliable performance over long periods, reduced maintenance and high durability. Steel roadside barriers are prone to corrosion and other compromises to their functionality. Therefore, using high anti-corrosion steel material is now seen as a viable solution to this problem. Thus, the objective of this paper is to expand the scope of applications for high anti-corrosion steel material for roadside barriers. This paper assesses the impact safety such as structural performance, occupant protection performance and post-impact vehicular response performance by a simulation review on roadside barriers built with high strength anti-corrosion steel materials named as hot-dip zinc-aluminium-magnesium alloy-coated steel. The simulation test results for the roadside barriers built with high strength anti-corrosion steels with reduced sectional thickness meet the safety evaluation criteria, hence the proposed roadside barrier made by high strength and high anti-corrosion hot-dip zinc-aluminium-magnesium alloy-coated steel will be a good solution to serve safe impact performance as well as save maintenance cost.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1997.10a
• /
• pp.310-315
• /
• 1997

An extensive corrosion study was initiated by galvalume steel sheet manufacturing company to clarify the corrosion behavior of zinc and zinc and zinc-alloy coated automotive sheet steel in out panel and electrical application. Since the early 1980's the use of zinc and aluminum alloy coated steel for vehicular corrosion protection has increased drastically. This paper describes the evaluation of formability, weldability and painted corrosion performance of galvalume steel sheet. This paper presents an overview of the program and some initial test results on the weldability, lifetime of the electrode tip shape of the spot welding and corrosion protection. Galvalume steel sheet improved corrosion performance and spot weldability of galvalume steel has no problem for the variation of welding current. And tip lifetime was changed according to the influence of shape.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2009.06a
• /
• pp.397-398
• /
• 2009

• Journal of Welding and Joining
• /
• v.23 no.3
• /
• pp.76-82
• /
• 2005

Recently the application of laser welding technology has been considered to shipbuilding structure. However, when this technology is applied to primer coated steel, good quality weld beads are not easily obtained. Because the primer-coated layer caused the spatter, humping bead and porosity which are main part of the welding defect attributed to the powerful vaporizing pressure of zinc. So we performed experiment with objectives of understanding spatter and porosity formation mechanism and producing sound weld beads in 6mmt primer coated steels by a $CO_2$ CW laser. The effects of welding parameters; defocused distance, welding speed, coated thickness and coated position; were investigated in the bead shape and penetration depth on bead and lap welding. Alternative idea was suggested to suspend the welding defect by giving a reasonable gap clearance for primer coated thickness. The zinc of primer has a boiling point that is lower than melting point of steel. Zinc vapor builds up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Significant effects of primer coated position was lap side rather than surface. Therefore introducing a small gap clearance in the lap position, the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, formation and suspension mechanism of the welding defects was suggested by controling the factors.

• 제어로봇시스템학회:학술대회논문집
• /
• 1996.10b
• /
• pp.836-839
• /
• 1996

Throughout CGL (Continuous Galvanizing Line) in steel works, zinc-coated steel sheets are produced which are used where long-running corrosion resistivity is required. During the galvanizing process, top dross is created and floated on the zinc pot. Because the dross leaves ill patterns on the coated sheets, a robot system is developed to automatically collect and remove the top dross. It consists of a robot and its carriage system, a pot level sensor, a system controller, and special robot tools. For the first time the level of zinc pot must be measured and fed back to the robot controller to avoid submersion of the robot hand into the hot zinc pot. In this paper, acoustic distance sensor is tested as a candidate for the pot level sensor in the view point of hot environment. Some considerations on the use of the acoustic distance sensor will be denoted.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.2
• /
• pp.74-80
• /
• 1998

An extensive corrosion study was initiated by galvalume steel sheet manufacturing company to clarify the corrosion behavior of zinc and zinc-alloy coated automotive sheet steel in out panel and electrical application. Since the early 1980's the use of zinc and aluminum alloy coated steel for vehicular corrosion protection has increased drastically. This paper describes the evaluation of formability, weldability and painted corrosion performance of galvalume steel sheet. This paper presents an overview of the program and some initial test results on the weldability, lifetime of the electrode tip shape of the spot welding and corrosion protection. Galvalume steel sheet improved corrosion performance and spot weldability of galvalume steel sheet has no problem for the variation of welding current. And tip lifetime was changed according to the influence of shape.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.20 no.2
• /
• pp.145-150
• /
• 2011

There is problem to reduce the car body weight for improving fuel consumption and $CO_2$ generation. As one of the solution, the multi material car body concept using aluminum alloys and high strength steels is proposed recently. Therefore, new welding processes by which these dissimilar material can be joined in high reliability and productivity are demanded. Laser spot welding was developed for joining of dissimilar metals. In the present work, Laser spot welding of zinc coated steel and aluminum alloy was investigated, and the process parameters were studied. Otherwise, the influences of process parameters on the weldability, the formation of intermetallic compound layer and the mechanical properties have been investigated. When intermetallic compound layer thickness was more than 1mm, specimen was failure in the interface.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.316-321
• /
• 2003

The spatter and porosity could be occurred during $CO_2$ CW laser welding of Primer-coated Steel for Shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate has caused the spatter, humping bead and porosity and these are main part of the welding defect, attributed to the powerful vaporizing pressure of primer attached on the base metal. The zinc of primer has a boiling point that is the lower temperature than melting point of steel. Zinc va}X)f will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position, the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.

• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.1
• /
• pp.109-115
• /
• 2004

The spatter and porosity could be occurred during$CO_2$CW laser welding of Primer- coated steel for shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate induced the spatter humping bead and porosity and these are main part of the welding defect. attributed to the powerful vaporizing pressure of primer attached on the base metal The zinc of Primer has a boiling point that is the lower temperature than melting point of steel zinc vapor will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position. the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.

• Corrosion Science and Technology
• /
• v.10 no.6
• /
• pp.199-204
• /
• 2011

Hot dip metallic coated steels like as galvanized (GI), zinc-aluminium (GL) and aluminium coated steels are mostly used where corrosion resistance is needed. There are two kinds (type 1 and type 2) of aluminium coated steel being commercially used among them. Type 1 aluminium coated steel is coated with an Al-5~11 wt%Si alloy and Type 2 aluminium coated steel consists of commercially pure aluminium. Type 1 Al coated steel is generally used in automotive components and electrical appliances while type 2 aluminium coated steel is mainly used in construction applications such as building cladding panels, air conditioning and ventilation system. In this study, Type 1 aluminium coated steels have tested by accelerated conditions (salt spray or corrosive gas) and outdoor exposure condition in order to understand their corrosion behaviour. Due to the distinct corrosion mechanism of Al which exposes to the severe chloric condition, Salt Spray Test cannot predict the ordinary atmospheric corrosion of Al based coated materials. In addition, the test results and their corrosion feature of Al coated steel sheets will be discussed comparing with other metallic coated steel sheets of GI and GL.