• Journal of the Korean Wood Science and Technology
• /
• 제13권4호
• /
• pp.67-72
• /
• 1985

To improve the bending strength of sawdustboard, verious resin contents of 10, 13, 16, and 19% were applied to the thin shell (face layer) composed with wire net or not. The shell effect of sawdust and wire net composition formed with core sawdustboard were evaluated. Forcusing on the effects of wire net composition and noncomposition including a comparison with chipboard and veneer complyboard, bending properties (Modulus of rupture (MOR), Modulus of elasticity (MOE), Stress at proportional limit ($S_{pl}$). Work to maximum load ($W_{ml}$))were analyzed and discussed. 1. In modulus of rutpute, veneer comply was the highest (621.5 kg/$cm^2$), and next decreasing order was wire net composition (159.1 kg/$cm^2$), chipboard (81.75 kg/$cm^2$), and wire net noncomposition (76.21 kg/$cm^2$) as in modulus of elasticity, work to maximum load, except for stress at proportional limit. 2. The highly significant effects were shown in both wire net composition and noncomposition, at the same time wire net composition exceeded two times of noncomposition throughout resin contents in bending properties. Chipboard was similar to the mean or 16% resin content in noncomposirion. 3. Every board in wire net composition above 10% resin content was beyond 100 kg/$cm^2$ in MOR, minimum allowable strength for structural use according to KS F 3104. In conclusion, the feasibility for improving the bending strength of weak sawdustboard by wire net composed shell was offered.

• 한국기계가공학회지
• /
• 제11권5호
• /
• pp.129-136
• /
• 2012

On this study, $CO_2$ gas, net of Ar gas, and mixed gas in solid wire(AWS ER 70S-6) and flux cored wire(AWS E71T-1) were used to weld on Mild steel(SS400). After the progress, the status changes of the welds in Mild steel(SS400) were investigated with compositional changes. For stable experiments, welding was conducted using the automatic feeder. Radiation testing, hardness testing, chemical composition analysis and penetrated cross-section were measured. Through these experiments, shapes of penetrated cross-section, chemical composition changes, and weld defects according to the variation of welding gas were known. Weld defects and weld cross-sectional shapes by the variation of the welding voltage were also detected.