• 한국재료학회지
• /
• 제12권11호
• /
• pp.856-859
• /
• 2002

To investigate effects of heat treatments including grain size control in substrate aluminum on nanopore arrays in anodic alumina template, aluminum was heat treated at $500^{\circ}C$ for 1h. The heat treated aluminum was anodized by two successive anodization processes in oxalic solution and the nanopore arrays in anodic alumina layer were studied using TEM and FE-SEM. The highly ordered porous alumina templates with 110 nm interpore distance and 40 nm pore diameter have been observed and the pore array of the anodic alumina has a uniform and closely-packed honeycomb structure. In the case of alumina template obtained from heat treated aluminum substrate, the well- ordered nanopore region in anodic alumina increased and became more homogeneous compared with that from non-heattreated one.

• 분석과학
• /
• 제23권3호
• /
• pp.233-239
• /
• 2010

폴리스테린을 주형으로 사용하여 순수한 매크로포러스 실리카 지지체를 졸겔법에 의하여 제조하였으며, 은 입자가 매크로 기공 안에 균일하게 분산되어 있는 매크로포러스 은/실리카 복합소재를 성공적으로 제조하였다. 순수한 실리카 다공체는 폴리스테린 크기에 따라 100 nm와 200 nm의 균일한 기공을 가지고 있었으며 이는 폴리스테린의 크기에 따라 기공크기를 제어할 수 있었다. 매크로포러스 은/실리카 기공의 크기 제어와 $AgNO_3$의 농도에 따른 미세구조를 관찰한 결과 TEOS의 3 wt% $AgNO_3$를 사용한 것이 가장 이상적인 균일한 기공의 분포를 나타내었다. 매크로포러스 은/실리카 복합체는 100-200nm 균일한 기공을 가지고 있었으며, 지지체 내의 은 입자는 대략 15~20 nm 크기를 보여주었다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2002년도 International Meeting on Information Display
• /
• pp.697-700
• /
• 2002

Porous anodic aluminum oxide(AAO) templates prepared by anodizing method were used for growing multiwalled carbon nanotubes(CNTs). AAO templates with the homogeneous pore diameter and length were obtained by two step anodizing technique. Using AAO templates, vertically well-ordered two-dimensional carbon nanotube arrays were fabricated. We investigated the field emission property of CNTs grown using different catalyst metals in vacuum chamber (<$10^{-7}$ Torr) on AAO Template. To explain the different emission property, the surface reaction between catalysts and alumina pores which inserted carbon species of $C_2H_2$ using High resolution transmission electron microscopy (HRTEM) was studied.

• 한국결정학회:학술대회논문집
• /
• 한국결정학회 2002년도 정기총회 및 추계학술연구발표회
• /
• pp.49-49
• /
• 2002

A strategy for the synthesis of more stable and large periodic mesoporous organo-silica materials has been developed for the 2D hexagonal mesoporous organosilica by the core-shell approach using nonionic PEO-PLGA-PEO triblock copolymer templates. The BET surface area of the solvent-extracted hexagonal mesoporous organosilica is estimated to be 1,016 ㎡/g and the pore volume, pore diameter, and wall thickness are 1.447 ㎤/g, 65 Å, and 43 Å, respectively. More hydrophobic PLGA block than the PPO block used for templates of mesoporous silica proves to be quite effective in confining the organosilicates within the PEO phase. Reaction temperature and acid concentration of an initial solution as well as the chemical nature of the bloc k copolymer templates also demonstrate to be important experimental parameters for ordered organosilica mesophase. Moreover, the mesoporous organosilicas prepared with the PEO-PLGA-PEO block templates maintain their structural integrity for up to 25 days in boiling water at 100℃. The mesoporous materials with large pores and high hydrothermal stability prepared in this study has a potential for many applications.

• 콘크리트학회논문집
• /
• 제16권2호
• /
• pp.277-282
• /
• 2004

In a hardened concrete, diffusion of oxygen, carbon dioxide, aggressive ions, and moisture from the environment to the concrete takes place through the pore network. It is well known that making dense cement matrix enhances the durability of concrete as well as all the characteristics including strength of concrete. In this paper,9 mix concretes with water to cementitious material ratio (40,45, and $50\%$) and replacement ratio of GGBFS (40 and $60\%$ of cement by weight) were studied on the micro-pore structure by mercury intrusion porosimetry and the accelerated chloride diffusion test by potential difference. From the results the average pore diameter and accelerated chloride diffusivity of concrete were ordered NPC > G4C > G6C. It is concluded that there is a good correlation between the average pore diameter and the chloride diffusivity, and the mineral admixtures has a filling effect, which increases the tortuosity of pore and makes large pores finer, on the pore structure of cement matrix due to the latent hydraulic reaction with hydrates of cement.

• 구강회복응용과학지
• /
• 제25권2호
• /
• pp.183-190
• /
• 2009

본 연구의 목적은 NaF와 $H_3PO_4$를 사용하여 양극산화과정을 통해 나노튜브 제작 조건을 찾는 것이다. 절삭된 직경 15 mm, 두께 1.5 mm의 티타늄 디스크를 양극에, 백금을 음극에 연결하고 전극간의 거리는 10 mm가 되도록 하였다. $H_3PO_4$와 NaF 용액을 전해질로 하여 양극산화를 시행하였는데 전압, 전해질 농도, 산화시간을 달리하여 티타늄 디스크에 나노튜브를 형성하였다. 양극산화 후 24시간 동안 증류수로 세척한 후 24시간 동안 $40^{\circ}C$ 오븐에서 건조하고 시편의 표면구조 형상을 관찰 분석하였다. 실험 결과 0.5 wt % NaF에서 전압과 시간이 증가함에 따라 pore 형태의 초기 나노튜브 형성되었다. 1.0 wt % NaF에서 20 V, 20 분과 25 분에서 나노튜브가 생성되었고, 30 V에서 튜브의 형태가 커지면서 터지는 양상을 보였다. 2.0 wt % NaF에서 전압과 시간에 상관없이 적절한 나노튜브형태가 형성되지 않았다. $1M\;H_3PO_4$, 1.0 wt % NaF 전해용액, 20 V, 20분 양극산화 조건에서 티타늄 디스크 상에 가장 잘 정렬된 형태의 나노튜브 구조가 형성되었다. 양호한 형태의 나노튜브 형성을 위해서는 전해질의 종류에 따라 적절한 농도, 전압, 시간의 형성조건이 필요할 것으로 사료된다.

• Korean Chemical Engineering Research
• /
• 제47권5호
• /
• pp.608-614
• /
• 2009

본 연구에서는, 비이온성 삼원공중합체 계면활성제인 $EO_{20}PO_{70}EO_{20}$를 주형으로 사용해, 다양한 Si/Ru 몰 비의 루테늄이 치환된 SBA-15들(Ru-SBA-15)을 합성하였다. 촉매 또는 선택적 흡착제 등으로써의 응용가능성을 검토하기 위해 Ru-SBA-15의 질소 또는 산소 흡착/탈착 거동을 조사하였다. Ru-SBA-15의 기공 크기는 Barrett-Joyner-Halenda(BJH) 및 Broekhoff-de Boer/Frenkel-Halsey-Hill isotherm(BdB-FHH) 방법($D_{BdB-FHH}$)을 이용하여 결정하였다. Si/Ru 비율이 50/1인 Ru-SBA 15의 $D_{BJH}$와 $D_{BdB-FHH}$는 각각 3.9, 4.7 nm였다. 투과전자현미경(TEM) 관찰에 의해 Si/Ru의 몰비율이 50인 Ru-SBA 15의 기공 크기는 4.7 nm로 나타났고, 이것은 BdB-FHH 방법을 사용한 $N_2$ 흡착 결과와 일치하였다. 산소 흡착/탈착 등온선으로부터 얻은 Brunauer-Emmett-Teller(BET) 기공 표면적은 질소의 흡착/탈착 등온선으로부터의 기공 표면적보다 높았는데, 각각 $612.7m^2/g$, 그리고 $573.3m^2/g$이었다. X선 회절(XRD) 패턴과 TEM 분석에 의해 본 연구에서 합성한 Ru-SBA-15는 잘 정렬된 육방정계 정렬을 가지는 것을 알 수 있었다.