• Proceedings of the Korean Society of Laser Processing Conference
• /
• 2004.10a
• /
• pp.82-85
• /
• 2004

• Journal of Welding and Joining
• /
• v.34 no.3
• /
• pp.17-22
• /
• 2016

In terms of mechanical and metallurgical characteristics, the effect of tool plunge depths(0.2, 0.5, 0.7, 1.0, 1.5mm) on weldability in dissimilar Al5083-O/DP590 friction spot joint has been clarified. From the results, it is found that the stirred nugget was stably formed at a plunge depth of more than 0.7mm, which is caused by improved stirring action against each other material. With increasing a plunge depth, the thickness of intermetallic compound(IMC) layer in Al5083-O/DP590 joint has a tendency to increase. The tensile shear strength reaches to the maximum failure load of 6.5kN at a plunge depth of 0.7mm due to relatively small decrease in the thickness of Al5083-O sheet and relatively minute thickness of IMC layer, compared with those of other plunge depth conditions.

• Journal of Welding and Joining
• /
• v.24 no.6
• /
• pp.39-43
• /
• 2006

A ferritic stainless steel, STS430, and a galvanized steel for case and frame of electronic goods are welded by resistance spot welding and resistance projection welding methods. In this study, resistance spot welding has been performed to investigate the weldability of dissimilar materials such as a ferritic stainless steel and a galvanized steel. Tensile load of the spot weld without heat treatment was 196 kN and brittle fracture occurred at interface between STS430 and nugget due to the high hardness, 380 Hv, in nugget. It was found that the hardness of as-welded nugget increased with higher cooling rate during resistance spot welding by comparing with GTA weld of same materials. Heat treatment by applying second current made nugget softened. Tensile load of heat treated weld increased and reached to 303 kN and fracture occurred at base metal, a galvanized steel.

• Journal of Welding and Joining
• /
• v.13 no.1
• /
• pp.127-137
• /
• 1995

The possibility of new GMAW process using economic shielding gases including CO$_{2}$ gas was investigated on the effect of shielding gas on weldabilty. In the optimum welding condition using 600A power source, FCAW process showed low depositions rate, 114 g/min at 300A, but new GMAW using other mixed shielding gases exhibited high deposition rate, 208-224 g/min at 450A. TIME gas, Ar+CO$_{2}$ gas and Ar+CO$_{2}$+O$_{2}$ gas as a shielding gas were able to be used to the very high welding current(450A), moreover TIME gas and Ar+CO$_{2}$ gas showed the highest arc stability among shielding gases studied in this experiments. The weld penetration was performed by axial spray transfer mode of weld droplet. On the basis of workability, weldability and economic point of view, Ar mixture (80%Ar+20%CO$_{2}$) gas was recommended as a shielding gas for the development and application of new GMAW process. This shielding gas showed the low spatter, good weld quality, stable arc and low cost at the region of high welding current.

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.1
• /
• pp.30-41
• /
• 2006

This paper shows mechanical Properties and behaviors of macrostructures for specimens welded by F.S.W according to welding conditions and tool dimensions with $6.35mm_t$ aluminum 7075-T651 alloy plate. It apparently results in defect-free weld zone in case transition speed was changed to 15mm/min 61mm/min and 124mm/min under conditions of tool rotation speed such as 800rpm. 1250rpm and 1600rpm respectively with tool's Pin diameter 40mm and 60mm. The optimum mechanical property, ultimate stress,${\sigma}_Y=470Mpa$ is obtained at the condition of 124mm/min of travel speed with 800rpm of tool rotation speed using full screw type pin. shoulder dia. $20{\phi}mm$ pin dia. $6{\phi}mm$ and pin length 6mm. The full-screw type and the half-screw type pin shows the similar behaviors of weldability. It is found that the size of nugget is depended on tool transition speed and tool dimension by macrostructures of the cross section of weld zone.

• Journal of Welding and Joining
• /
• v.22 no.5
• /
• pp.53-57
• /
• 2004

Friction stir weldability of AZ31B-H24, AZ61A-F and AZ91C-F Mg alloys were studied using microstructural observation and mechanical tests. The microstructure of stir zone(SZ) was coarse in AZ31B-H24 alloy whereas it was very fine both in AZ61A-F and AZ91C-F alloys. The hardness of SZ was remarkably increased by very fine recrystallized grains both in AZ61A-F and AZ91C-F alloys. On the other hand, the hardness of SZ was decreased in AZ31B-H24 due to the coarse microstructure. In SZ, AZ91C-F alloy showed very high hardness values because of dispersion hardening of $Mg_{17}$Al$_{12}$($\beta$ phase) and Al solid solution hardening. Because of more $Mg_{ 17}Al_{12}($\beta$ phase)$ intermetallic compounds, Mg alloy with high Al content showed poor mechanical properties.s.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1317-1321
• /
• 2007

Aluminized steel sheet that Al coated on low carbon steel has a excellent heat resistance, thermal reflection and corrosion resistance. It has applied to fuel tank, automotive exhaust systems, etc. Laser weldability of the aluminized steel for the full penetration welding will be described in this paper. We focused on the effect of Al coating conditions on weld strength. For these objectives, aluminized steel sheets that has various thickness and coating weight were prepared for laser welding. And then, tensile-shear and hardness test were carried out. At that same time, Al content mixed in weld after laser welding was evaluated and investigated a correlation between the mixed Al and mechanical properties. Besides, as removing partially coating layer, weldability has been investigated according to position of coating layer. As a result of this study, as increasing Al content in weld, tensile-shear strength was decreased. Also it was identified that Al of coating layer caused grain growth.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1322-1327
• /
• 2007

Many automotive companies have tried to apply the aluminum alloy sheet to car body because reducing the car weight can improve the fuel efficiency of vehicle. In order to do that, sheet materials require of weldablity, formability, productivity and so on. Aluminum alloy was not easy to join these metals due to its material properties. Thus, the laser is good heat source for aluminum alloy welding because of its high heat intensity. However, the welding quality was not good by porosity, underfill, and magnesium loss in welded metal for AA5182 aluminum alloy. In this study, Nd:YAG laser welding of AA 5182 with filler wire AA 5356 was carried out to overcome this problem. The weldability of AA5182 laser welding with AA5356 filler wire was investigated in terms of tensile strength and Erichsen ratio. For full penetration, mechanical properties were improved by filler wire. In order to optimize the process parameters, model to estimate tensile strength by artificial neural network was developed and fitness function was defined in consideration of weldability and productivity. Genetic algorithm was used to search the optimal point of laser power, welding speed, and wire feed rate.

• Journal of Welding and Joining
• /
• v.22 no.6
• /
• pp.19-24
• /
• 2004

The laser welding and its analysis of thin-sheet carbon steels were carried out with high power $CO_{2}$ laser. The main factor of weld quality of laser welding is gap and edge quality. This work was preformed to focus on the gap tolerance problem during laser welding. First, bead on plate welding of thin sheet was examined to investigate the effect of laser welding variables, and to obtain optimum welding condition. Butt welding was also carried out to show the effect of gap on the laser weldability of thin sheet. In order to investigate the effect of gap on formability of welded thin sheet, LDH test was caried out. At high welding speed, the partial penetration was obtained by low heat input. Otherwise, porosity was formed in the bead at low weld speed because of too much heat input. The optimum welding condition of welding was derived from bead width, penetration and hardness property. The maximum gap tolerance on laser welding was observed to be about 0.2mm. This gap size has good relationship with beam size of laser spot(about 0.3mm). The formability of welded sheet was about $80{\%}$ value of base metal and the gap size has not affected on the formability, although weld quality is dependent on the gap size.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.107-112
• /
• 2002

Ferritic stainless steels would be the most important alloys under the chloride environment. They are a cheaper alternative to austenitic stainless steels [1]. The present study is related to gas tungsten arc welding (GTAW) characteristics of Type 444 stainless steels. The heat of welding leads to grain coarsening in the HAZ and in the weld metal of ferritic stainless steels because they solidify directly from the liquid to the ferritc phase without any intermediate phase transformation. It is therefore recommended that these alloys be welded with a low heat input and at high welding speeds. Attempts to improve weldability were made by using of direct current straight polarity (DCSP) and pulsed current GTAW processes in this study. Measuring weld bead, grain size and Erichsen test were performed and the effects of heat input, pulse frequency on the weld metal and HAZ were studied. The main results were obtained as followings: decreasing heat input was effective to control the width of weld both in DCSP welding and in pulsed current welding; pulsed current welding was found to refine the grain size effectively and the finest grain size was found at the frequency of 150Hz in pulsed current welding; it was found that decreasing heat input also refine the HAZs effectively and the frequency had no different effect on HAZ at the same heat input; the ductility could be improved effectively in pulsed current welding.